Summary

Assembly and Characterization of Polyelectrolyte Complex Micelles

Published: March 02, 2020
doi:

Summary

We provide protocols and representative data for designing, assembling, and characterizing polyelectrolyte complex micelles, core-shell nanoparticles formed by polyelectrolytes and hydrophilic charged-uncharged block copolymers.

Abstract

Polyelectrolyte complex micelles (PCMs), core-shell nanoparticles formed by self-assembly of charged polymers in aqueous solution, provide a powerful platform for exploring the physics of polyelectrolyte interactions and also offer a promising solution to the pressing problem of delivering therapeutic oligonucleotides in vivo. Developing predictive structure-property relationships for PCMs has proven difficult, in part due to the presence of strong kinetic traps during nanoparticle self-assembly. This article discusses criteria for choosing polymers for PCM construction and provides protocols based on salt annealing that enable assembly of repeatable, low-polydispersity nanoparticles. We also discuss PCM characterization using light scattering, small-angle X-ray scattering, and electron microscopy.

Introduction

When oppositely charged polyelectrolytes are mixed in aqueous solution, entropy gain from release of their counterions causes demixing of the solution into a polymer-rich condensed phase and a polymer-depleted supernatant1,2,3,4,5, a phenomenon known as polyelectrolyte complexation. If a neutral hydrophilic block is conjugated to one or both of the polyelectrolytes, nanoscale phase separation occurs instead (Figure 1A). The resulting self-assembled core-shell nanoparticles are variously referred to as polyelectrolyte complex micelles (PCMs), polyion complex micelles, block ionomer complexes, or coacervate-core micelles by analogy to surfactant micellization, even though all components of the system are hydrophilic6,7. A PCM's ability to encapsulate hydrophilic molecules such as proteins and nucleic acids, as well as the extensive tunability offered by the block copolymer carrier architecture makes them attractive candidates for delivering therapeutic molecules in vivo8,9,10,11,12,13.

Delivering therapeutic nucleic acids to cellular targets is a particularly important challenge, and one for which PCMs offer several advantages. Therapeutic nucleic acids (genetic DNA, mRNA, and oligonucleotides such as siRNA) have immense potential for improving human health, but must overcome numerous biological and physical barriers to realize that potential14,15,16. Bare nucleic acids are degraded by serum and cellular nucleases, are quickly cleared from circulation, and their strong negative charge makes it difficult for them to penetrate cell membranes without assistance. Current approaches for overcoming these barriers include costly chemical modifications to prevent damage from nucleases and/or encapsulation into various lipid nanoparticles assembled via hydrophobic interactions15,17,18. While these methods have proven effective for local injections and liver targeting, systemic use presents significant limitations of toxicity, immunogenicity, and limited biodistribution16. By contrast, PCMs use the negative charge of nucleic acids to condense them within the phase-separated core, while the neutral corona provides a steric barrier against degradation as well as a platform for incorporating ligands to enhance targeting or internalization11,19. In vitro and animal studies have shown that PCMs can effectively deliver various nucleic acid payloads20,21,22,23,24, but weaknesses in our ability to predict PCM properties such as size, shape, and stability from the properties of the constituent polymers have hindered their wider adoption.

Recent work by our group and others in the field has begun to address this problem by developing structure-property, and in some cases structure-property-function relationships for PCMs formed from nucleic acids and various cationic-neutral polymers7,25,26,27. Two consistent themes that have emerged from these studies are the importance of developing well-controlled, repeatable protocols for PCM assembly and the benefit of using multiple techniques to characterize the resulting nanoparticles. Polyelectrolytes, particularly those with high charge density like nucleic acids, interact with each other very strongly, and appear to readily become kinetically trapped upon mixing, resulting in PCM preparations that are highly sensitive to small variations in procedure and display high polydispersity and poor repeatability from batch to batch. PCMs have also been shown to adopt a wide range of shapes and sizes depending on the atomic-level configurations of their components, and capturing this diversity with any individual characterization technique is very difficult, particularly since some common techniques such as dynamic light scattering (DLS) require assumptions about particle shape for their interpretation.

In this article, we discuss material design and selection for PCMs, with a focus on oligonucleotides and cationic-neutral diblock copolymers. We then describe a salt annealing protocol that uses high salt concentrations followed by slow dialysis to avoid kinetic trapping during PCM assembly. The polyelectrolytes are mixed in high salt conditions where electrostatic attractions are screened, then the salt concentration is slowly lowered to allow the polyelectrolytes to settle into their most energetically favorable configurations, analogous to the slow cooling process of thermal annealing. Using this protocol, we are regularly able to achieve exceptionally low polydispersity and high repeatability for oligonucleotide PCMs7,26. Finally, we describe how four separate measurement techniques can be used to characterize PCMs over a very wide range of length scales, from external morphology to internal structure: DLS, multi-angle light scattering (MALS), small angle X-ray scattering (SAXS), and transmission electron microscopy (TEM). We hope that these protocols will enable more researchers to effectively explore the capabilities of these interesting nanoparticles.

Polymer Selection and Preparation
PCM properties are strongly influenced by the physical and chemical characteristics of the constituent polymers, making polymer selection a critical step in the design process. The most well-characterized block copolymers for nucleic acid PCMs are linear diblocks such as poly(lysine)-poly(ethylene glycol) (pLys-PEG), but PCMs can be formed between polyelectrolytes and a variety of hydrophilic neutral-charged polymers, which can be generated in a high throughput manner28. The choice of charged group strongly affects the stability of ion pairing and shape of micelles26, and PCM size has been shown to increase with the length of the charged block5,7,26 (Figure 2), thus allowing PCM properties to be tuned for the requirements of a desired application. For linear diblocks, we have found that the charged block should have at least 10 charges and be strongly charged at the desired pH. Longer charged blocks may promote PCM formation with oligonucleotides such as siRNA, which are difficult to complex with shorter blocks21. We have successfully observed PCM formation with block lengths up to 200, and the literature describes longer polymers. More flexibility is available in the choice of neutral blocks24, but experience has shown that very short neutral blocks lead to aggregation rather than nanoparticle formation, and that the minimum neutral length increases with charged block length. For pLys-PEG, a PEG MW of at least 3,000–5,000 is required for pLys lengths below ~50, and longer lengths are required as the charged block is increased further. Increased neutral block length results in increased PCM size, particularly shell thickness, due to steric crowding of the neutral polymers.

This manuscript presents a protocol for preparing PCMs from lyophilized high-purity pLys-PEG and oligonucleotides of known quantity, but should be readily adaptable to other systems as well. We have tested it successfully with several charged polypeptides, including polyarginine and polyglutamic acid, as well as several synthetic polyelectrolytes, such as polyacrylic acid and poly(vinylbenzyl trimethylammonium). We also describe preparing PCMs with a stoichiometric ratio of polyelectrolyte charges, but this is easily modified. We find it easiest to work in charge concentration units (c.c.), which also naturally accommodates polymers that are not fully charged. If either polymer is not well-characterized, care should be taken to accurately determine the polymer lengths/masses and ensure that excess salt is not present beyond that needed for charge neutralization by dialysis, for example. The presence of any retained water should also be accounted for when concentrations are calculated. Nucleic acid concentration can be conveniently quantified by absorbance at 260 nm, and the presence or absence of terminal phosphates should be considered when calculating the c.c.

When using oligonucleotides as polyanions, the hybridization state and chemical structure help determine the propensity for self-assembly and the characteristics of the resulting PCM5,7,26. Optimizing these, within the requirements for biological efficacy if using PCMs for delivery, will increase the likelihood of forming the desired structures. Helpful tools for analyzing hybridization include MATLAB functions for nucleic acids, NUPACK29, and IDT OligoAnalyzer. We recommend analyzing a candidate sequence to understand the strength of binding to 1) itself in a hairpin formation; 2) another copy of the same sequence (self-dimer); and 3) to other oligonucleotides present in the system. DNA and RNA melting temperatures for a specific sequence can also be calculated using the nearest-neighbor method30,31. Thermal annealing of nucleic acids (step 2.3) denatures any residual secondary structure in the individual nucleotides and promotes equilibrium folding.

PCM Characterization and Analysis
A wide range of techniques are available for characterizing nanoparticles, including static and dynamic light scattering, small angle scattering of electrons or neutrons, and electron microscopy. In this article, we provide protocols for two light scattering techniques, small angle X-ray scattering, and two electron microscopy techniques.

DLS measures the autocorrelation of temporal fluctuations in scattering intensity at one angle from Brownian motion of the sample. Fitting this data can provide hydrodynamic radius and polydispersity for spherical micelles (Figure 3). Multiple angle light scattering (MALS) measures the static scattering intensity at many angles. This angular dependence describes the shape of the nanoparticle but is limited to length scales longer than ~50 nm for visible light, which limits its effectiveness for smaller nanoparticles. Both techniques are based on refractive index mismatch and primarily describe the outside dimensions of the nanoparticle.

Small angle X-ray scattering (SAXS) uses X-rays as the scattering probe, and their shorter wavelength allows measurements over a range of ~0.1–100 nm. Fitting the observed scattering intensity vs. angle (conventionally expressed as momentum transfer q) provides information on PCM morphology (i.e., size and shape) and also internal structure. If an absolute intensity calibration is available, and if the scattering intensity can be extrapolated to zero angle, PCM mass and aggregation number can also be estimated32, making SAXS an extremely versatile and valuable method. Small angle neutron scattering (SANS) is sensitive over a similar range of length scales but is only available at specialized facilities and will not be explicitly discussed in this article33,34,35.

Recent years have seen the advent of benchtop SAXS instruments, but we find that synchrotron sources are better suited for PCM characterization, as their higher intensity allows data to be collected much faster for these low-contrast samples. We provide a brief protocol for acquiring PCM SAXS data at Beamline 12-ID-B at the Advanced Photon Source (Argonne National Laboratory, USA) from a user perspective. This protocol should be applicable to most synchrotron sources, but consulting with local staff before proposing an experiment is highly recommended. We also provide a data reduction and analysis protocol using Irena36, a free set of macros written for Igor Pro. Irena includes a versatile set of form factors for modeling SAXS data and allows for construction of multicomponent models that are capable of describing the complex scattering profile of PCMs (see Representative Results, Figure 4). Irena also has comprehensive documentation and tutorials available online. Before attempting the procedures below, we recommend familiarization with these, particularly the tutorial "Modeling of SAXS data with two main scatterer populations".

Radiation damage is a concern for X-ray scattering, but several measures can be employed to minimize it. In particular, we recommend using a flow cell setup with a syringe pump and PCM sample flowing during data acquisition, rather than a sealed capillary. This also greatly simplifies background subtraction. We also suggest taking multiple exposures of the flowing sample rather than one longer one in order to limit the flux that any single volume of sample sees and to allow for comparison of the exposure data to identify any damage.

In contrast to the scattering techniques, which generally require fitting to interpret, transmission electron microscopy (TEM) provides a real space visual image of the nanoparticles by passing an electron beam through the sample and projecting an image on a scintillation screen (Figure 5). We present protocols for two TEM techniques in this article. Cryo TEM freezes micelle samples into a thin layer of vitreous ice, preserving structural conformation with minimal foreign substances, optimal for micelles ≤~10-100 nm in radius. Negative stain TEM uses a heavy metal salt (e.g., uranium) to surround the sample after it has been dried on the surface of a grid. The dense stain will scatter more electrons than the sample, adding contrast and producing a negative image of the sample. Cryo TEM is recommended for high-quality images. However, it is more costly, time consuming, and may not provide sufficient contrast. When this is a concern, negative stained samples should be used. Examples of each are shown in Figure 5.

Each of these techniques reports on slightly different aspects of the nanoparticles, with different strengths and limitations. Light scattering is readily available, and is often the fastest approach, but has substantial limitations in size and shape resolution. SAXS can provide information over a large range of length scales at reasonably high throughput, but requires specialized equipment to acquire the data, as well as modeling to interpret it. TEM images are straightforward to interpret but can be limited in contrast and are inherently low throughput. Our experience has shown that using multiple techniques for characterization greatly increases the information that can be obtained about PCM properties and simplifies interpretation of data sets obtained from each one alone. For example, SAXS and TEM primarily examine a PCM's dense core, while light scattering reports on the overall dimensions of the nanoparticle. Thus, combining them allows measurement of both core and corona size. TEM's ability to acquire real space images can provide ground truth data to enable selection of appropriate form factors for modeling SAXS data that might otherwise be ambiguous. This article describes protocols for all four techniques, and an example process for using them to characterize an unknown sample is given in the Discussion section.

Protocol

1. Preparation of Materials Weigh out lyophilized diblock polymer and add water up to nearly the volume required for a stock solution of 10 mg/mL final concentration. Vortex at maximum speed for 2 min. Sonicate for 5 min. Very long diblocks may require additional sonication. The stock solution should appear completely transparent and homogeneous. Adjust pH to 7.4 using NaOH or HCl as needed. Add water to the final volume. pLys-PEG solutions are fairly stable but should be refrigerated for …

Representative Results

In order to illustrate the characterization methods described above, we show typical results for PCMs assembled from oligonucleotides and block copolymers of various lengths and chemistries (Figure 1). Figure 2 provides an example of how PCM core size (as determined from SAXS and TEM, Figure 4 and Figure 5) varied with charged block length. Figure 3 shows DLS data and fitti…

Discussion

As mentioned above, the protocols presented here are written with a focus on oligonucleotides as the polyanion component and pLys-PEG as the cationic-neutral block copolymer, but we have tested them with a variety of polymers, such as poly(acrylic acid), polyglutamate, and PEG-poly(vinylbenzyl trimethylammonium), and believe they will be generally applicable for most polyelectrolyte pairs. One parameter that may need to be optimized is the salt concentration used for annealing, because it should be high enough that PCMs …

Disclosures

The authors have nothing to disclose.

Acknowledgements

We thank Phil Griffin and Tera Lavoie of the Soft Matter Characterization Facility and Advanced Electron Microscopy Facility, respectively, at The University of Chicago. We also thank Xiaobing Zuo and Soenke Seifert of the Advanced Photon Source at Argonne National Laboratory and NIST Center for Hierarchical Materials Design (CHiMaD) for support. We thank Jeff Ting and Michael Lueckheide for their contributions to this work.

Materials

70 mm circle filter paper Whatman 1001-070 Filter paper for wicking during grid prep
Carbon Film TEM grid Electron Microscopy Sciences CF200-Cu TEM grid
DAWN Wyatt Technology DAWN MALS instrument
DNA oligonucleotide Integrated DNA Nanotechnologies Inc Custom oligonucleotide
Lacey Carbon TEM grid Electron Microscopy Sciences LC200-Cu TEM grid
Methoxy-poly(ethylene glycol)-block-poly(l-lysine hydrochloride) PEG5k – PLKC50 Alamanda Polymers Inc mPEG5K-b-PLKC50 Example block copolymer
Milli-Q Millipore Sigma Ultrapure water
NanoDrop Thermo Scientific For measuring nucleic acid concentration
negative-action tweezers Dumont N7 Tweezers for grid preparation
Parafilm "M" Bemis Company Inc PM996 Laboratory film
Quantifoil Holey Carbon TEM grid Electron Microscopy Sciences Q210CR1.3 TEM grid
Research Goniometer and Laser Light Scattering System Brookhaven Instruments BI-200SM DLS/MALS instrument
Slide-A-Lyzer G2 2K 0.5 mL Thermo Scientific Pierce Protein Biology 87723 Dialysis cartridge
small volume cuvette Brookhaven Instruments BI-SVC Cuvette for DLS/MALS
Solarus 950 Advanced Plasma System Gatan Solarus 950 Plasma system for TEM grids
Talos TEM FEI Talos TEM used for cryo samples
Tecnai Spirit TEM FEI Spirit TEM used for dry samples
Uranyl Formate SPI-Chem 16984-59-1 For negative staining samples for TEM
Vitrobot FEI Vitrobot Vitrification robot for cryo grid preparation

References

  1. Spruijt, E., Westphal, A. H., Borst, J. W., Cohen Stuart, M. A., van der Gucht, J. Binodal compositions of polyelectrolyte complexes. Macromolecules. 43 (15), 6476-6484 (2010).
  2. van der Gucht, J., Spruijt, E., Lemmers, M., Cohen Stuart, M. A. Polyelectrolyte complexes: bulk phases and colloidal systems. Journal of Colloid and Interface Science. 361 (2), 407-422 (2011).
  3. Priftis, D., Laugel, N., Tirrell, M. Thermodynamic characterization of polypeptide complex coacervation. Langmuir. 28 (45), 15947-15957 (2012).
  4. Fu, J., Schlenoff, J. B. Driving Forces for Oppositely Charged Polyion Association in Aqueous Solutions: Enthalpic, Entropic, but Not Electrostatic. Journal of the American Chemical Society. 138 (3), 980-990 (2016).
  5. Vieregg, J. R., et al. Oligonucleotide-Peptide Complexes: Phase Control by Hybridization. Journal of the American Chemical Society. 140 (5), 1632-1638 (2018).
  6. Voets, I. K., de Keizer, A., Cohen Stuart, M. A. Complex coacervate core micelles. Advances in Colloid and Interface Science. 147-148, 300-318 (2009).
  7. Lueckheide, M., Vieregg, J. R., Bologna, A. J., Leon, L., Tirrell, M. V. Structure-Property Relationships of Oligonucleotide Polyelectrolyte Complex Micelles. Nano Letters. 18 (11), 7111-7117 (2018).
  8. De Kruif, C. G., Weinbreck, F., de Vries, R. Complex coacervation of proteins and anionic polysaccharides. Current Opinion in Colloid & Interface Science. 9 (5), 340-349 (2004).
  9. Vieregg, J. R., Tang, T. Y. D. Polynucleotides in cellular mimics: Coacervates and lipid vesicles. Current Opinion in Colloid & Interface Science. 26, 50-57 (2016).
  10. Marciel, A. B., Chung, E. J., Brettmann, B. K., Leon, L. Bulk and nanoscale polypeptide based polyelectrolyte complexes. Advances in Colloid and Interface Science. 239, 187-198 (2017).
  11. Cabral, H., Miyata, K., Osada, K., Kataoka, K. Block Copolymer Micelles in Nanomedicine Applications. Chemical Reviews. 118 (14), 6844-6892 (2018).
  12. Tan, Z., et al. Block Polymer Micelles Enable CRISPR/Cas9 Ribonucleoprotein Delivery: Physicochemical Properties Affect Packaging Mechanisms and Gene Editing Efficiency. Macromolecules. 52 (21), 8197-8206 (2019).
  13. Horn, J. M., Kapelner, R. A., Obermeyer, A. C. Macro- and Microphase Separated Protein-Polyelectrolyte Complexes: Design Parameters and Current Progress. Polymers. 11 (4), 578 (2019).
  14. Juliano, R. L. The delivery of therapeutic oligonucleotides. Nucleic Acids Research. 44 (14), 6518-6548 (2016).
  15. Kanasty, R., Dorkin, J. R., Vegas, A., Anderson, D. Delivery materials for siRNA therapeutics. Nature Materials. 12 (11), 967-977 (2013).
  16. Lorenzer, C., Dirin, M., Winkler, A. M., Baumann, V., Winkler, J. Going beyond the liver: progress and challenges of targeted delivery of siRNA therapeutics. Journal of Controlled Release. 203, 1-15 (2015).
  17. Allen, T. M., Cullis, P. R. Liposomal drug delivery systems: from concept to clinical applications. Advanced Drug Delivery Reviews. 65 (1), 36-48 (2013).
  18. Li, W., Szoka, F. C. Lipid-based nanoparticles for nucleic acid delivery. Pharmaceutical Research. 24 (3), 438-449 (2007).
  19. Miyata, K., Nishiyama, N., Kataoka, K. Rational design of smart supramolecular assemblies for gene delivery: chemical challenges in the creation of artificial viruses. Chemical Society Reviews. 41 (7), 2562-2574 (2012).
  20. Oishi, M., Nagasaki, Y., Itaka, K., Nishiyama, N., Kataoka, K. Lactosylated poly(ethylene glycol)-siRNA conjugate through acid-labile ss-thiopropionate linkage to construct pH-sensitive polyion complex micelles achieving enhanced gene silencing in hepatoma cells. Journal of the American Chemical Society. 127 (6), 1624-1625 (2005).
  21. Christie, R. J., et al. Targeted polymeric micelles for siRNA treatment of experimental cancer by intravenous injection. ACS Nano. 6 (6), 5174-5189 (2012).
  22. Kuo, C. H., et al. Inhibition of atherosclerosis-promoting microRNAs via targeted polyelectrolyte complex micelles. Journal of Materials Chemistry B. 2 (46), 8142-8153 (2014).
  23. Ge, Z., et al. Targeted gene delivery by polyplex micelles with crowded PEG palisade and cRGD moiety for systemic treatment of pancreatic tumors. Biomaterials. 35 (10), 3416-3426 (2014).
  24. Van Bruggen, C., Hexum, J. K., Tan, Z., Dalai, R. J., Reineke, T. M. Nonviral Gene Delivery with Cationic Glycopolymers. Accounts of Chemical Research. 52 (5), 1347-1358 (2019).
  25. Hayashi, K., et al. Influence of RNA Strand Rigidity on Polyion Complex Formation with Block Catiomers. Macromolecular Rapid Communications. 37 (6), 486-493 (2016).
  26. Marras, A. E., Vieregg, J. R., Ting, J. M., Rubien, J. D., Tirrell, M. V. Polyelectrolyte Complexation of Oligonucleotides by Charged Hydrophobic-Neutral Hydrophilic Block Copolymers. Polymers. 11 (1), 83 (2019).
  27. Phillips, H. R., et al. Glycopolycation-DNA Polyplex Formulation N/P Ratio Affects Stability, Hemocompatibility, and in Vivo Biodistribution. Biomacromolecules. 20 (4), 1530-1544 (2019).
  28. Ting, J. M., Wu, H., Herzog-Arbeitman, A., Srivastava, S., Tirrell, M. V. Synthesis and Assembly of Designer Styrenic Diblock Polyelectrolytes. ACS Macro Letters. 7 (6), 726-733 (2018).
  29. Zadeh, J. N., et al. NUPACK: Analysis and design of nucleic acid systems. Journal of Computational Chemistry. 32 (1), 170-173 (2011).
  30. Santa Lucia, J. A unified view of polymer, dumbbell, and oligonucleotide DNA nearest-neighbor thermodynamics. Proceedings of the National Academy of Sciences of the United States of America. 95 (4), 1460-1465 (1998).
  31. Xia, T., et al. Thermodynamic parameters for an expanded nearest-neighbor model for formation of RNA duplexes with Watson-Crick base pairs. Biochemistry. 37 (42), 14719-14735 (1998).
  32. Orthaber, D., Bergmann, A., Glatter, O. SAXS experiments on absolute scale with Kratky systems using water as a secondary standard. Journal of Applied Crystallography. 33 (2), 218-225 (2000).
  33. Srivastava, S., et al. Gel phase formation in dilute triblock copolyelectrolyte complexes. Nature Communications. 8, 14131 (2017).
  34. Lindhoud, S., et al. Salt-induced disintegration of lysozyme-containing polyelectrolyte complex micelles. Langmuir. 25 (19), 11425-11430 (2009).
  35. Lindhoud, S., de Vries, R., Schweins, R., Stuart, M. A. C., Norde, W. Salt-induced release of lipase from polyelectrolyte complex micelles. Soft Matter. 5 (1), 242-250 (2009).
  36. Ilavsky, J., Jemian, P. R. Irena: tool suite for modeling and analysis of small-angle scattering. Journal of Applied Crystallography. 42 (2), 347-353 (2009).
  37. Sambrook, J., Fritsch, E. F., Maniatis, T. . Molecular Cloning: a Laboratory Manual. , (1989).
  38. Jakeš, J. Regularized positive exponential sum (REPES) program-A way of inverting laplace transform data obtained by dynamic light scattering. Collection of Czechoslovak Chemical Communications. 60 (11), 1781-1797 (1995).
  39. Schillen, K., Brown, W., Johnsen, R. M. Micellar Sphere-to-Rod Transition in an Aqueous Triblock Copolymer System – a Dynamic Light-Scattering Study of Translational and Rotational Diffusion. Macromolecules. 27 (17), 4825-4832 (1994).
  40. Provencher, S. W. Contin – a General-Purpose Constrained Regularization Program for Inverting Noisy Linear Algebraic and Integral-Equations. Computer Physics Communications. 27 (3), 229-242 (1982).
  41. Provencher, S. W. A Constrained Regularization Method for Inverting Data Represented by Linear Algebraic or Integral-Equations. Computer Physics Communications. 27 (3), 213-227 (1982).
  42. Sarachan, K. L., Curtis, J. E., Krueger, S. Small-angle scattering contrast calculator for protein and nucleic acid complexes in solution. Journal of Applied Crystallography. 46 (6), 1889-1893 (2013).
  43. Beaucage, G. Approximations leading to a unified exponential power-law approach to small-angle scattering. Journal of Applied Crystallography. 28 (6), 717-728 (1995).
  44. Marras, A. E., Vieregg, J. R., Ting, J. M., Rubien, J. D., Tirrell, M. V. . Materials Data Facility. , (2018).
  45. Modena, M. M., Rühle, B., Burg, T. P., Wuttke, S. Nanoparticle Characterization: What to Measure. Advanced Materials. , (2019).
  46. Mourdikoudis, S., Pallares, R. M., Thanh, N. T. K. Characterization techniques for nanoparticles: comparison and complementarity upon studying nanoparticle properties. Nanoscale. 10 (27), 12871-12934 (2018).

Play Video

Cite This Article
Marras, A. E., Vieregg, J. R., Tirrell, M. V. Assembly and Characterization of Polyelectrolyte Complex Micelles. J. Vis. Exp. (157), e60894, doi:10.3791/60894 (2020).

View Video