Enhanced Electron Injection and Exciton Confinement for Pure Blue Quantum-Dot Light-Emitting Diodes by Introducing Partially Oxidized Aluminum Cathode
Please note that all translations are automatically generated. Click here for the English version.

酸化アルミニウムの陰極の電子注入と部分的に導入することで純粋な青色量子ドット発光ダイオードの励起子閉じ込め

DOI:
10.3791/57260-v

•

10:41 min

•

May 31, 2018

•

, , , , , , , ,
1State Key Laboratory of Alternate Electrical Power System with Renewable Energy Sources,North China Electric Power University, 2Department of Mathematics,Quaid-I-Azam University, 3NAAM Research Group, Faculty of Science,King Abdulaziz University

Chapters

  • 00:05Title
  • 01:03Indium Tin Oxide (ITO) Glass Patterning and Cleaning
  • 03:20Fabrication of a Hole Injection Layer (PEDOT:PSS), a Hole Transport Layer (Poly-TPD), and an Emissive Layer (ZnCdS/ZnS QDs)
  • 06:03Vacuum Deposition and Autoxidation of Aluminum Electrodes
  • 07:18Results: Characterization and Performance Evaluation of Blue QD-LED Devices
  • 09:09Conclusion

Summary

Automatic Translation

Automatic Translation

アルミ、白ネズミの陰極を採用することにより高パフォーマンス、純粋な青 ZnCdS/ZnS 系量子ドット発光ダイオードを製造するためのプロトコルが表示されます。

Tags

Quantum-dot Light-emitting DiodesElectron InjectionExciton ConfinementPartially Oxidized Aluminum CathodeITO Glass PreparationEtchingCleaningFabrication Process

Article

Embed

ADD TO PLAYLIST

Usage Statistics

Related Videos

分子適合体とクラスターの空間的分離

予測研究および拡張の3D可視化のためのスケーラブルなNanohelices

気孔率に複製技術とエフェクトでオープンセルアルミフォームの製造のためのプロトコルのキャスト

多粒子フォノン閉じ込めモデルとラマン分光法を用いて、ナノ結晶のサイズ分布の特性

エキシプレックスからの安定した発光と白色発光電気化学セルの作製

ブルーハザードフリーキャンドルライトのOLED

反応速度と私の燃焼ダイナミクス<sub> 4</sub> O<sub> 9</sub>とアルミニウムの混合物

キャストアルミ部品の暖かいスピニングのための実験手順

光共振器およびレーザ応用のためのポリマーマイクロスフェアの作製

直交の励起と検出を用いた平面キャビティ内 InGaAs 量子ドットの共鳴蛍光

Read Article