资料来源: 布莱克斯堡弗吉尼亚理工大学土木与环境工程系罗伯特. 里昂
混凝土是最常见的建筑材料之一, 包括两个阶段: 砂浆阶段, 包括混凝土, 水和空气, 和骨料相组成的粗和细骨料。在设计混凝土组合时有两个关键的考虑因素。首先, 混凝土必须是可行的, 易于铸造的形式, 在其新鲜的情况下, 即使在形式包装钢筋。在这种情况下, 混凝土的流变性是重要的。第二, 混合料必须在28天 (或类似规定的时间) 内生产出具有一定强度的硬化混凝土, 并提供良好的可维护性。
在本实验中, 本文将探讨一种以试批法命名的混凝土配合比的方法。所生产的混凝土将用于进行典型的试验, 以确定新鲜混凝土的主要特征, 包括坍落度, 流动性, 空气含量和密度。试验批处理方法是一种简单、经验性的混合设计方法。
本实验的目的是: (1) 使用试验批次组合法确定骨料、水泥和混凝土的水的最佳配比, 以满足特定的坍落度要求, (2) 在实验室中学习混凝土搅拌实践环境, (3) 观察新鲜混凝土的特性, 并 (4) 准备 4 “x8” 混凝土钢瓶进行后续评价。
In general, mixes such as the one described above will have slumps of 3 to 4 inches. Such values are common for small jobs with little steel congestion in the forms. In modern construction, the widespread use of superplasticizers has meant that it is economical to get much higher slumps (6 to 10 inches, i.e., self-leveling concrete). Non-air-entrained mixes will show air contents below 2%, while air-entrained mixes, depending on admixture dosage, will show 5% to 8% air content. The unit weight of normal-weight concretes is around 145 to 150 pounds per cubic foot, but concrete made with lightweight aggregates (i.e., expanded shales) may be as light as 100 to 120 pounds per cubic foot.
Slump cone and flow table tests are in-situ test results used to determine if the concrete being delivered to the site has the specified workability. These tests are meant to ensure an adequate rheology for the mix, i.e., a good initial "viscosity" that lasts long enough for the concrete to get from the batching plant to its final position in the forms without leaving large voids or similar defects around the reinforcement. Additionally, the air-content test is key to ensuring long-term durability in areas where freeze-thaw cycles occur. It should be noted that all of these tests are at best an attempt to determine quantities that are difficult to measure under the best of circumstances. Under the time pressure and chaos of a work site, these tests provide indirect measures of important short- and long-term properties.
The test described herein is used every day in thousands of construction sites in the United States and across the world. The main application for a test of this type is to provide quality control and quality assurance. Some of the test cylinders cast in this laboratory will be cured under specified conditions (fog room curing at 73.5+3.5oF and 100% relative humidity) and tested at 28 days to determine if the mix design was appropriate. The relatively high temperature and humidity ensures that most of the cement will hydrate, thus the w/c ratio for this mix will provide strong and durable concrete. This experimental work ensures that batching plants meet the required specifications. Some of the test cylinders will be cured at ambient conditions at the work site to determine how fast the in-situ concrete is curing. On site, the development of strength is tied mostly to temperature and humidity conditions, which are random and can vary substantially over a 28-day period. To offset these conditions, the concept of concrete maturity is used often. The maturity of the concrete is calculated in degree days, generally summing the number of days times the difference between the average daily temperature and a reference temperature (generally 32oF). When the number of degree-days reaches one thousand, the concrete is assumed to have reached its intended strength.
Concrete is one of the most common construction materials in use today. Before you can pour your concrete and build your structure, you need to determine if the concrete mixture is suitable for the particular application.
Concrete consists of two phases, a mortar phase comprised of cement, water, and air, and an aggregate phase comprised of coarse and fine aggregates. When designing a concrete mixture, we need to ensure that the fresh concrete has an adequate rheology in order for it to be easily workable. The trial batch method is used to determine the characteristics of fresh concrete. This in situ test is meant to ensure that the concrete mixture at the batching plant has the same viscosity when it arrives at the construction site and is poured in forms.
This video will discuss the main properties of concrete and illustrate how fresh concrete mixtures are tested in the laboratory.
The trial method begins with samples of cement, water, coarse and fine aggregates, and target air content. The coarse and fine aggregates are assumed to be inert. The main variables we need to consider are the cement, water, and air. The water-to-cement ratio is very important because the strength of concrete is directly dependent on this quantity.
Concrete’s strength is customarily measured at 28 days after casting and typically varies in terms of water-to-cement ratio from about 0.35 for high-strength concrete to about 0.6 for low-strength concrete.
A lower water-to-cement ratio decreases the permeability of concrete by reducing the penetration rates of salt ions into concrete and thus the corrosion of the concrete reinforcement. High curing temperature and humidity significantly accelerate the strength gains.
The air content of a fresh concrete mixture plays an important role in durability, especially for concrete used in regions that undergo cycles of freezing and thawing. Free water expands as it freezes and turns to ice and can crack the concrete. The air bubbles in the mix allow this expansion without cracking the concrete. A higher amount of air results in a lower strength, so for a given strength a higher water-to-cement ratio is necessary.
Strength and durability are long-term properties of concrete. The short-term properties such as workability need to be taken into account as well. In the next step of the trial method, coarse and fine aggregates are added to the mixture to achieve the desired plastic consistency. The amount of coarse aggregate and sand will be adjusted during batching to achieve adequate workability and slump for the concrete mix.
The slump, or concrete’s flowability, measures the consistency before the concrete sets. The slump test consists of pouring and compacting fresh concrete into an inverted cone in three layers. Once the cone is filled, the cone is lifted and the amount that the concrete slumps or subsides is measured. Results of the slump test are an indication of the cohesiveness of the mix. A well-proportioned mix will fall but retain its original shape. A poor mix will crumble, segregate, and fall apart.
Now, let’s look at the concrete mixing practices in a laboratory environment and learn how the trial batch method is used to prepare concrete test cylinders for subsequent applications.
Weigh out and separately store the given quantities of coarse aggregates, fine aggregates, cement, and water. Record the exact weights on the data sheet. Before you begin mixing, dampen the inside of the mixer and all of the tools so that they are wet without leaving any standing water.
Now, put the coarse and fine aggregates into the mixture with about one-fifth of the water. Allow these components to mix for about two minutes. With the mixer still rotating, add the cement and additional water in five to 10 small increments. When you have finished adding these components, let them mix for another five minutes and then turn the mixer off. You are now ready to test the slump of the concrete mix.
Dampen the slump cone and place it in the mixing pan with the large diameter down. Hold the slump cone down firmly against the pan, and then fill about one-third of the volume with a layer of concrete. Tamp the layer with 25 strokes distributed uniformly over the cross-section of the cone. When you are finished, add two more layers of concrete, tamping each layer so that the rod penetrates slightly into the previous layer. Strike off the excess concrete so that the cone is completely filled but not overflowing.
Immediately lift the cone carefully and vertically to separate it from the concrete, then determine the slump by measuring the difference between the height of the mold and the height of the concrete. The slump of this mixture should be between three and four inches. If it is too low or the mix appears harsh and does not flow properly, gradually add small, measured quantities of fine or coarse aggregate as appropriate, then thoroughly re-mix and re-test the concrete until the desired slump and consistency are achieved.
Now that the mixture is correct, weigh the remaining aggregates and record these values in the data sheet. Compute the actual amounts of coarse and fine aggregates used in the concrete mix from the initial weights.
Finally, determine the unit weight of this concrete mix. Record the weight of an empty, 1 cubic-foot container and then fill the container with concrete following the same procedure used to fill the slump cone. Weigh the full container and calculate the unit weight for this mix by subtracting the empty container weight.
Prepare four cylindrical molds for casting the test samples. Measure and record the empty weight of each mold on the data sheet. Fill each mold by following the same procedure used to fill the slump cone in the previous section. After filling each mold, measure and record the filled weight on the data sheet.
Cover the molded concrete with a plastic bag to prevent evaporation of water from the mixture. Leave the test cylinders to set for 16 to 32 hours, and then strip the disposable plastic molds from the concrete specimens.
Finally, place the cylinders in the curing environment. In this case, the cylinders are left to cure in ambient conditions.
Now that you understand how to determine the characteristics of fresh concrete, let’s review the results.
The quantities and materials used in this experiment to prepare the concrete mixture are shown in this table. Our fresh concrete mix had a slump of 3.5 inches. In general, mixes such as the one described in this experiment have slumps of three to four inches. Such values are common for small jobs with little steel congestion in the forms.
The unit weight of our concrete was 147 pounds per cubic foot. The unit weight of normal weight concretes is around 145 to 150 pounds per cubic foot, but concrete made with lightweight aggregates, expanded shales, for example, may be as light as 100 to 120 pounds per cubic foot.
The water-to-cement ratio for our concrete batch is 0.45. This ratio indicates that the compressive strength of our test cylinders at 28 days will be around 5,000 psi. This ratio also indicates that the durability of our concrete makes it suitable to exposure to freezing and thawing in moist conditions or deicers.
The trial batch method is used on many construction sites around the world to test batches of concrete. This simple test ensures consistent quality control and assurance at the work site.
Superplasticizers are chemical additives that considerably reduce the viscosity of a fresh concrete mix for a short period of time in order to allow for ease of placement into the forms. In modern construction, the widespread use of superplasticizers has meant that it is economical to get much higher slumps, in the 6 to 10 inch range, corresponding to self-leveling concrete.
Air-entrainment agents are chemicals that create many small, well-dispersed air bubbles and provide the spaces necessary for free water inside the concrete mixture to expand during freezing without cracking the concrete. Air-entrainment testing of fresh concrete is device-specific. For example, pressure is applied to the sample to compress the entrained air in the pores. The device uses the change in air volume to determine the air content of the mix. Non-air-entrained mixes will show air contents below 2%, while air-entrained mixes, depending on the additive’s dosage, will show 5 to 8% air content.
You’ve just watched JoVE’s introduction to tests on fresh concrete. You should now understand how the trial batch method is used to determine the optimal proportions of aggregates, cements, and water to prepare concrete that meets slump requirements.
Thanks for watching!