An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature
Please note that all translations are automatically generated. Click here for the English version.

Une Technique disponible pour la préparation de nouveaux MnCuNiFeZnAl coulé avec Superior Service capacité et à haute température d’amortissement

6,759 Views

•

14:51 min

•

September 23, 2018

DOI:

10.3791/57180-v

DOI:
10.3791/57180-v

•

14:51 min
September 23, 2018

•

1 Views
, , , , ,
1School of Manufacturing Science and Engineering,Sichuan University, 2Department of Mechanical Engineering,Hong Kong Polytechnic University, 3Department of Mechanical and Electrical Engineering,Chengdu Aeronautic Polytechnic

Summary

Automatically generated

Nous présentons ici un protocole pour obtenir un alliage à base de Mn-Cu avec d’excellentes performances globales par une technologie de fusion de haute qualité et méthodes de traitement de chaleur raisonnable du roman.

Explore More Videos

Cast MnCuNiFeZnAl AlloyDamping CapacityHigh Service TemperatureVacuum Induction MeltingSand Mold CastingHeat TreatmentMicrostructureManganese-copper Based AlloysFace-centered Cubic To Face-centered Tetragonal Phase TransformationAging TreatmentNanoscale Precipitates

Read Article

Cite this Article

Li, D., Liu, W., Li, N., Zhong, Z., Yan, J., Shi, S. An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature. J. Vis. Exp. (139), e57180, doi:10.3791/57180 (2018).