Predicting Catalyst Extrudate Breakage Based on the Modulus of Rupture
Please note that all translations are automatically generated. Click here for the English version.

破壊係数をに基づいて推定触媒押し出し破損

DOI:
10.3791/57163-v

•

09:53 min

•

May 13, 2018

•

, , , ,
1Process Technology Department, Catalyst Technology Division,ExxonMobil Research and Engineering Company

Capítulos

  • 00:04Título
  • 01:02Bending Strength Measurements
  • 03:14Aspect Ratio Measurements
  • 04:26Catalyst Collision (Drop) Test
  • 05:54Bulk Crush Testing
  • 07:42Results: Analysis of Catalyst Extrudate Breakage Data
  • 09:01Conclusion

Summary

Tadução automática

Tadução automática

ここで表面に対して衝突すること固定層における圧縮によって押し出し触媒の破断や当該触媒押の破損の弾性率を測定するためのプロトコルを提案する.

Tags

Catalyst ExtrudateModulus Of RuptureBending StrengthBreakageCollisionStressFixed BedRupture ForceExtrudate ResilienceBending Test FrameAnvil SpeedSupport SpanMaximum ForceBuchner FunnelNitrogen Gas BlanketRupture Force Reading

Article

Embed

ADICIONAR À PLAYLIST

Usage Statistics

Vídeos Relacionados

ウィスパリングギャラリーモード共振器に基づいたマイクロ波フォトニクスシステム

液体環境におけるパルスUVレーザー照射によるシリコン表面の濡れ性の選択エリア変更

特徴付けインフィールド歩行者の行動に基づいて、人間によって誘発される振動のシミュレーション

グラフェンナノプレートレットとマルチスケール複合材料強化に基づくひずみセンシング

フレキシブル有機単結晶ベースの電界効果トランジスタの電気的特性に曲げの影響

モジュラー設計と閉ループ制御戦略に基づく知能ロボットの生産

横 NIPIN フォト トランジスタを用いた柔軟な画像センサーの作製

部分最小二乗回帰による近赤外分光法に基づくO-クレゾール濃度オンライン測定

刺激されたラマン散乱に基づく非線形顕微鏡の実施

混相a-VOxに基づく非対称クロスバーのバイアスと作製を用いたSitu透過電子顕微鏡

Read Article