Synthesizing Sodium Tungstate and Sodium Molybdate Microcapsules via Bacterial Mineral Excretion

Pao-Hung Lin; Ying-Tang Huang; Fu-Wen Lin

doi:10.3791/57022

JoVE Journal > Chemistry

Química

Synthesizing Sodium Tungstate and Sodium Molybdate Microcapsules via Bacterial Mineral Excretion

Published: January 30, 2018

doi:

10.3791/57022

Pao-Hung Lin¹, Ying-Tang Huang², Fu-Wen Lin³

¹Department of Electronic and Computer Engineering,National Taiwan University of Science and Technology, ²Department of Marine Biotechnology,National Kaohsiung Marine University, ³Institute of Applied English,National Taiwan Ocean University

Summary

This work presents a protocol for manufacture sodium tungstate and sodium molybdate microcapsules via bacteria and their corresponding nanoparticles.

Abstract

We present a method, the bacterial mineral excretion (BME), for synthesizing two kinds of microcapsules, sodium tungstate and sodium molybdate, and the two metal oxides' corresponding nanoparticles—the former being as small as 22 nm and the latter 15 nm. We fed two strains of bacteria, Shewanella algae and Pandoraea sp., with various concentrations of tungstate or molybdate ions. The concentrations of tungstate and molybdate were adjusted to make microcapsules of different length-to-diameter ratios. We found that the higher the concentration the smaller the nanoparticles were. The nanoparticles came in with three length-to-diameter ratios: 10:1, 3:1 and 1:1, which were achieved by feeding the bacteria respectively with a low concentration, a medium concentration, and a high concentration. The images of the hollow microcapsules were taken via the scanning electron microsphere (SEM). Their crystal structures were verified by X-ray diffraction (XRD)—the crystal structure of molybdate microcapsules is Na₂MoO₄ and that of tungstate microcapsules is Na₂WO₄with Na₂W₂O₇. These syntheses all were accomplished under a near ambient condition.

Introduction

Metal oxide nanoparticles are exploited for drug delivery¹, construction artificial bones², heterogeneous catalysis³, field emission⁴^,⁵, solar cells⁶, gas sensors⁷, and lithium batteries⁸. For practical applications, the mechanical strength of both nanocrystals and their microstructure are crucial. Among the microstructures, hollow shell structures can be used to create lightweight, mechanically robust materials⁹. Among hollow shell structures, a spherical shape is known to be more rigid than an ellipsoidal shape; the latter has a larger length-to-diameter ratio than the former¹⁰^,¹¹. This work describes a protocol for synthesizing spherical microcapsules via bacteria with a non-toxic method under an ambient condition, which contrasts with the alternative methods, including the template synthesis method¹², ultrasonic-spray-assisted synthesis method¹³ and hydrothermal method¹⁴. Some of the alternative methods require templates¹², some a temperature as high as 500 °C¹³, and some a high pressure¹⁴. As for the resulting structure, the template synthesis method utilizing the yeast template brings about a core-shell structure¹⁵, instead of one with a single wall, and the one utilizing the E. coli template produces a structure with length-to-diameter ratio of 1.7:0.8, and is not spherical.¹⁶.

In this work, we have made metal oxide microcapsules with a single wall and of spherical shape under an ambient condition by exploiting bacterial metabolism. In bacterial glycolysis, a chemical process that metabolizes carbon sources, like glucose and lactose, carbon sources are considered to be the origin of the reducing power generated therein. We manipulated bacterial metabolism by adjusting the concentration of carbon sources to achieve desired ends. This method is environment-friendly, using non-toxic agents and consuming much less electricity power. Lastly, this method allows the mass production of microcapsules simply by increasing the volume of broth.

Prior to the method, there have been another two methods utilizing bacterial metabolism to make minerals: biologically induced mineralization (BIM)¹⁷ and biologically controlled mineralization (BCM)¹⁸. Neither BIM nor BCM can be used for making sodium tungstate and molybdate tungstate microcapsules like our process, which is designated as the bacterial mineral excretion (BME)¹⁹. In this experiment, the shape of microcapsules can be controlled to have a length-to-diameter ratio from 10:1 to 1:1, and the size of nanoparticle grains that form the shells can be adjusted ranging from 15 nm to 110 nm.

Protocol

Caution: Use latex gloves, protective eyeglasses, and a laboratory coat for performing the experiment. Whenever using the biosafety cabinet, turn on the cabinet fan and keep the cabinet door half-closed.

1. Preparation of Glass Beads

Place 100 glass beads of 3 mm diameter in a 100-mL laboratory bottle, and then cap it tightly.
Autoclave the contents at 120 °C for 10 min.
Leave the bottle to cool down to room temperature, then place it in the biosafety cabinet.

2. Preparation of Lysogeny Broth (LB)

Dissolve 8 g powder of LB-Lennox broth in a 500-mL laboratory bottle with 400 mL of water.
Stir the contents with a PTFE magnetic stirring bar for 20 min, and then cap it tightly.
Autoclave the contents at 120 °C for 10 min.
Leave the solution to cool down to room temperature and place it in the biosafety cabinet.
Using a pipette, aliquot the broth into eight 15-mL centrifuge tubes in the biosafety cabinet (12.5 mL each).
Aliquot the remaining broth into three 100-mL laboratory bottles in the biosafety cabinet (100 mL each). Cap the three bottles tightly. Keep them in the biosafety cabinet.

3. Culture of Shewanella algae

Use the deep-frozen cryopreserved strain.
In the biosafety cabinet, pick out 1 mL of the frozen material from the frozen tube with a stainless-steel spatula, and place it into a centrifuge tube prepared in step 3.5.
Incubate the cultures for 24 h in a 37 °C incubator.

4. Preparation of LB-Lennox (Broth with Agar) Petri Dishes

Dissolve two tablets of LB-Lennox (broth with agar) into a 100-mL laboratory bottle with 100 mL of water.
Stir the contents with a PTFE magnetic stirring bar for 20 min and then cap it tightly.
Autoclave the contents at 120 °C for 10 min.
In the biosafety cabinet, aliquot by hand 100 mL of solution into 4 Petri dishes, ensuring each receive ~25 mL. Leave the solution to cool down to room temperature.

5. Preparation of Monoclonal Bacteria

In the biosafety cabinet, label the three bottles prepared in step 2.6, #1, #2 and #3, respectively.
Pipette 0.1 mL of the resultant bacterial suspension in step 3.3 into bottle #1. Cap the bottle and swing it by hand for 1 min to get a homogenous solution.
Pipette 0.1 mL of the resultant bacterial liquid in step 5.2 into bottle #2. Cap the bottle and swing it by hand for 1 min to get a homogenous solution.
Pipette 0.1 mL of the resultant bacterial liquid in step 5.3 into bottle #3. Cap the bottle and shake it by hand for 1 min to get a homogenous solution.
Pipette the liquid in bottle #3 into the 4 Petri dishes prepared in step 4.4, using a volume of 0.02 mL each.
Put the glass beads prepared in step 1.3 into the 4 Petri dishes used, 4 beads in each dish.
Close the lids of the Petri dishes and shake them by hand for 1 min.
Turn the Petri dishes upside down and incubate in a 37 °C incubator for 24 h.

6. Multiplication of Monoclonal Bacteria

Fetch 7 tubes prepared in step 2.5.
Pick out the resultant monoclonal bacteria from the 4 Petri dishes prepared in step 5.8 with a stainless steel-spatula, and put them into 7 tubes separately.
Leave the 7 tubes in a 37 °C incubator for 24 h.
Pick out the one with the largest light scattering using the visual colorimetric method.

7. Preparation of LB-Lennox Broth with Glucose and Salt

Put 10 g of LB-Lennox broth, 10 g of NaCl, and 10 g of glucose into a 500-mL laboratory bottle. Add water until the volume reaches 450 mL.
Stir the contents with a PTFE magnetic stirring bar for 20 min.
Autoclave the contents at 120 °C for 10 min.

8. Preparation of Sodium Tungstate

Put 16.5 g of Sodium Tungstate Na₂WO₄．2H₂O into a 100-mL laboratory bottle with a stainless-steel spatula. Add water until the volume reaches 50 mL.
Stir the contents with a PTFE magnetic stirring bar for 20 min.
Autoclave the contents at 120 °C for 10 min.
In the biosafety cabinet, get filtrate via a vacuum fiberglass filter with pores of 1 µm.

9. Preparation of LB with Glucose, Salt, and Sodium Tungstate

In the biosafety cabinet, pour the filtrate gained in step 8.4 by hand into the solution with glucose and salt prepared in step 7.3.
In the biosafety cabinet, aliquot with a pipette the 500 mL resultant solution in step 9.1 into 10 x 50 mL centrifuge tubes.

10. Culture of Bacteria

In the biosafety cabinet, fetch the liquid prepared in step 6.4 and aliquot it with a pipette into the 10 test tubes prepared in step 9.2, with each tube receiving 0.05 mL.
Incubate the 10 tubes in a 37 °C incubator for 120 h.

11. Harvest of BME minerals

Ultrasonicate each of the 10 tubes in step 9.2 at 20 KHz with 150 W for 1 h.
Centrifuge the tubes at 2,025 x g for 1 h.
Remove the clear liquid in the tubes with a pipette, add water, and then repeat steps 11.1 and 11.2 one more time.
Remove the clear liquid in the tubes with a pipette, add alcohol, and then ultrasonicate them at 20 KHz with 150 W for 1 h.
Centrifuge the tubes at 2,025 x g for 1 h.
Repeat steps 11.4 and 11.5 one more time
Harvest BME minerals by removing the clear liquid in the tubes with a pipette; afterwards, immediately cap the tubes without running any drying process.

12. Oscillating Temperature with Pandoraea sp. and Molybdate

Culture Pandoraea sp. in the same way as in steps 2, 3, 4, 5, and 6 for Shewanella algae. The result of this step corresponds to that of step 6.4.
Make LB broth with both glucose and salt in the same way as in steps 7, 8, and 9, except that the 16.5 g of sodium tungstate in step 7.1 is replaced with 12 g of sodium molybdate, Na₂MoO₄ · 2H₂O. The result of this step corresponds to that of step 9.2.
In the biosafety cabinet, fetch the liquid prepared in step 12.1, and aliquot it with a pipette into the 10 tubes prepared in step 12.2, with each tube receiving 0.05 mL.
Incubate the 10 tubes in step 12.3 under oscillating temperatures for 120 h in a reciprocal shaking bath, oscillating the temperature 5 times between 25 °C and 37 °C, with each temperature lasting for 12 h.

Representative Results

Figure 1 shows genuine spherical microcapsules. Both the two strains of bacterium, Shewanella algae and Pandoraea sp., originally have a length-to-diameter ratio of 3:1. For achieving the length-to-diameter ratio of 1:1, a high concentration (>100 mM) of metal oxyanions is required. A low concentration (<5 mM) of oxyanions can result in a length to diameter ratio of 10:1, as that in Figure 2, which may result from the influx of the oxyanions, blocking the binary fission of bacteria. Lastly, for achieving a length-to-diameter ratio of 3:1, like that in Figure 3, a medium concentration (~20 mM) of oxyanions is needed. The formation of spherical shells, with a length-to-diameter ratio of 1:1, may be brought about by bacterial drives that make themselves shrink their surface area to balance the intake of oxyanions while diffusing oxyanions through the cell membrane. The three figures together indicate the length-to-diameter ratio may be tuned to from 10:1 to 1:1 simply by adjusting the concentration of oxyanions.

Figure 4 and Figure 5 show the nanoparticle grains of sodium molybdate in different sizes: the smaller one being 15 nm, and the larger one 110 nm. Note that in Figure 5, on the non-shattered shells, particles of 110 nm can still be chained up to each other, forming porous shells. The larger one was gained through oscillating the temperature of the culturing broth 5 times between 25 °C and 37 °C, with each temperature lasting for 12 h. During the temperature oscillation, grains of different sizes can not only be produced but also maintain the micro-spherical structure, which means we can make microcapsules with different grain sizes, from 15 nm to 110 nm, just by controlling the broth temperature.

Figure 6 shows the broken wall with larger grains staying next to the opening of the wall. The wall thickness is about 22 nm and the larger grain is about 40-60 nm. The difference in size may result from different metabolic processes, which are not yet identified.

Figure 1: The SEM image of hollow spherical shells with a length-to-diameter ratio of 1:1. This structure was made of sodium tungstate excreted by Shewanella algae with glucose as the carbon source. Reprinted with permission from ECS J. of Solid State Sci. and Tech., 6(3), N3113 (2017). Copyright 2017, The Electrochemical Society. Please click here to view a larger version of this figure.

Figure 2: The SEM image of hollow long filament shells with a length-to-diameter ratio of 10:1. This structure was made of sodium molybdate excreted by Pandoraea sp. with glucose as the carbon source. Reprinted with permission from ECS J. of Solid State Sci. and Tech., 6(3), N3113 (2017). Copyright 2017, The Electrochemical Society. Please click here to view a larger version of this figure.

Figure 3: The SEM image of broken hollow rod-shaped shells with a length-to-diameter ratio of 3:1. This structure was made of sodium tungstate excreted by Shewanella algae with glucose as the carbon source. Reprinted with permission from ECS J. of Solid State Sci. and Tech., 6(3), N3113 (2017). Copyright 2017, The Electrochemical Society. Please click here to view a larger version of this figure.

Figure 4: The SEM image of shattered sodium molybdate shells with a grain particle size of 15 nm. Please click here to view a larger version of this figure.

Figure 5: The SEM image of shattered and non-shattered sodium molybdate shells with a grain particle size of 110 nm. Please click here to view a larger version of this figure.

Figure 6: The SEM image of broken hollow shells with a length-to-diameter ratio of 1:1. This structure was made of sodium tungstate excreted by Shewanella algae with glucose as the carbon source. Granules with a size about 40-60 nm hang outside the shell right next to a big hole, while the shell itself is made of granules with a size about 22 nm. Reprinted with permission from ECS J. of Solid State Sci. and Tech., 6(3), N3113 (2017). Copyright 2017, The Electrochemical Society. Please click here to view a larger version of this figure.

Discussion

Concerning the self-consistency of the experimental results, the preparation and multiplication of monoclonal bacteria are critical. This experiment, different from the template synthesis experiments¹⁵^,¹⁶, employed bioactive gram-negative bacteria. To get a single wall, we chose prokaryotic bacteria instead of eukaryotic bacteria like yeast¹⁵. To achieve a spherical shape with a length-to-diameter ratio of 1:1, instead of a larger length-to-diameter ratio¹⁶, we fed bacteria with a much higher concentration of oxyanions to manipulate them to shrink into a spherical shape, making microcapsules with a single, round, and thin wall (<30 nm).

Since the BME mainly relies on adjusting the concentration of oxyanions to control the metabolism of bacteria, it features two limitations. Firstly, the concentration of oxyanions is limited by the solubility, though the concentration should be as high as possible. Second, most bacterial metabolisms will stop at a temperature over 45 °C or under 5 °C, respectively the upper and lower bounds of our experiment.

Despite these two limitations, the BME has great potential for making metal oxide materials of practical interest. To substantiate this claim, we are going to try this method to make zirconium microcapsules and iron microcapsules—the former being a good candidate material for artificial bones, and the latter for drug delivery.

Declarações

The authors have nothing to disclose.

Acknowledgements

This work is supported by Ministry of Science and Technology, Taiwan, Republic of China, under grant number MOST 105-2221-E-011-008, and also by Advanced-Connectek Inc., Taipei, Taiwan, ROC under contract number RD Ref. No. 6749 and Dept. Ref. No. 011 through the Graduated Institute of Electro-Optical Engineering, National Taiwan University of Science and technology.

Materials

LB(Lennox)broth with agar tablets	Sigma-Aldrich	L7075	1 tablet for 50 mL broth with agar
LB (Lennox) broth	Sigma-Aldrich	L3022-1KG	LB (Lennox) powder 1 kg
Dextrose anhydrous	Nihon Shiyaku Reagent	PL 78695	glucose
Sodium Tungstate	Nihon Shiyaku Reagent	PL 76050	Na₂WO₄ · 2H₂O
Sodium Molybdate	Nihon Shiyaku Reagent	PL103564	Na₂MoO₄ · 2H₂O
Sodium Chloride	Nihon Shiyaku Reagent	PL 68131	NaCl
Ethanol 99.5%	Acros organics	AC615090040	CH₃CH₂OH
Water	Made in our university		de-ionlized water
Autoclave	Tomin Medical Equipmenco, Ltd., Taipei City, Taiwan, ROC	TM-329	heat to 120 °C for 10 min
Centrifuge	Digit System Laboratory System, New Taipei City, Taiwan, ROC	DSC302SD	centrifuge at 2025 x g
-80 °C Refrigerator	Panasonic	MDF-U3386S	Use to deep-freeze cryopreserve strain
Ultrasonic Homogenizer Sonicator Processor Cell Disruptor	Lenox	UPS-150	frequency 20 KHz power 150 W
Incubator	Customer made	custom made	heat to 40 °C or cool to 18 °C with time cotrol
Reciprocal shaking baths	Kingtech Scientific Co., Ltd	WBS-L
Digital Stirring Hot Plate	Corning	#6797-620D	use with PTFE magnetic stirring bar
Biosafety cabinet	Zong Yen co., LTD	ZYBH-420	All bacteria related process are done here
Scanning electron microscope	JEOL	JSM-6500F	SEM Images
50 mL centrifudge tube	Falcon	14-432-22
15 mL centrifudge tube	Falcon	14-959-53A
Laboratory bottle 100 mL	Duran	21 801 24 5
Laboratory bottle 500 mL	Duran	21 801 44 5
Stainless steel spatula	Chemglass	CG-1981-10
PTFE Disposable Stir Bars	Fisher	S68066
Plastic Petri Dishes	Fisher	S33580A
Shewanella algae	Courtesy of author #3	Courtesy of author #3
Pandoraea sp.	Courtesy of author #3	Courtesy of author #3

Referências

Chertok, B., Moffat, B. A., David, A. E., Yu, F., Bergemann, C., Ross, B. D., Yang, V. Iron Oxide Nanoparticles as a Drug Delivery Vehicle for MRI Monitored Magnetic Targeting of Brain Tumors. Biomaterials. 29 (4), 487 (2008).
Mansur, C., Pope, M., Pascucci, M. R., Shivkumar, S. Zirconia-Calcium Phosphate Composites for Bone Replacement. Ceramics Int. 24, 11 (1998).
Wang, Y., Arandiyan, H., Jason Scott, J., Bagheri, A., Dai, H., Amal, R. Recent advances in ordered meso/macroporousmetal oxides for heterogeneous catalysis: a review. J. Mater. Chem. A. 5, 8825 (2017).
Kleshch, V. I., Rackauskas, S., Nasibulin, A. G., Kauppinen, E. I., Obraztsova, E. D., Obraztsov, A. N. Field Emission Properties of Metal Oxide Nanowires. J. of Nanoelectron. and Optoelectron. 7, 35 (2012).
Ismagilov, R. R., Tuyakova, F. T., Kleshch, V. I., Obraztsova, E. A., Obraztsov, A. N. CVD nanographite films covered by ALD metal oxides: structural and field emission properties. Phys. Status Solidi C. 12 (7), 1022 (2015).
Mor, G. K., Shankar, K., Paulose, M., Varghese, O. K., Grimes, C. A. Use of Highly-Ordered TiO2 Nanotube Arrays in Dye-Sensitized Solar Cells. NANO LETT. 6 (2), 215-218 (2006).
Lee, J. -. H. Gas sensors using hierarchical and hollow oxide nanostructures: Overview. Sensors and Actuators B. 140, 319 (2009).
Poizot, P., Laruelle, S., Grugeon, S., Dupont, L., Tarascon Shankar, J. -. M. Nano-sized transition-metal oxides as negative-electrode materials for lithium-ion batteries. Nature. 407, 496 (2000).
Jang, D., Meza, L. R., Greer, F., Greer, J. R. Fabrication and deformation of three-dimensional hollow ceramic nanostructures. Nature Materials. 12, 893 (2013).
Lazarus, A., Florijn, H. C. B., Reis, P. M. Geometry-Induced Rigidity in Nonspherical Pressurized Elastic Shells. PRL. 109, 144301 (2012).
Vella, D., Ajdari, A., Vaziri, A., Boudaoud, A. Indentation of Ellipsoidal and Cylindrical Elastic Shells. PRL. 109, 144302 (2012).
Xu, H., Wang, W. Template Synthesis of Multishelled Cu2O Hollow Spheres with a Single-Crystalline Shell Wall. Angew. Chem. Int. Ed. 46, 1489 (2007).
Li, B., Shao, X., Hao, Y., Zhao, Y. Ultrasonic-spray-assisted synthesis of metal oxide hollow/mesoporous microspheres for catalytic CO oxidations. RSC Adv. 5, 85640 (2015).
Yu, J., Wang, G. Hydrothermal Synthesis and Photocatalytic Activity of Mesoporous Titania Hollow Microspheres. Powder Tech. 301, 96 (2016).
Xu, G., Zhang, X., Cui, H., Zhang, Z., Ding, J., Wu, J. Facile synthesis of mesoporous SnO2 microspheres using bioactive yeast cell. Powder Tech. 301, 96 (2016).
Nomura, T., Tanii, S., Ishikawa, M., Tokumoto, H., Konishi, Y. Synthesis of hollow zirconia particles using wet bacterial templates. Adv. Powder Tech. 24, 1013 (2013).
Frankel, R. B., Bazylinski, D. A. Biologically Induced Mineralization by Bacteria. Rev. in Mineralogy and Geochem. 54 (1), 95 (2003).
Bazylinski, D. A., Frankel, R. B. Biologically Controlled Mineralization in Prokaryotes. Rev. in Mineralogy and Geochem. 54 (1), 217 (2003).
Lin, P. -. H., Huang, Y. -. T., Lin, F. -. W. Sodium Tungstate and Sodium Molybdate Hollow Microspheres Biologically Controlled Mineralization in Prokaryotes. ECS J. of Solid State Sci. and Tech. 6 (3), N3113 (2017).

Play Video

PDF

DOI

DOWNLOAD MATERIALS LIST

Citar este artigo

Lin, P., Huang, Y., Lin, F. Synthesizing Sodium Tungstate and Sodium Molybdate Microcapsules via Bacterial Mineral Excretion. J. Vis. Exp. (131), e57022, doi:10.3791/57022 (2018).