Harvesting Solar Energy by Means of Charge-Separating Nanocrystals and Their Solids

1. Synthesis of ZnSe Core Nanocrystals⁸

1. Place 7.0 g ODA and a magnetic stir bar into a three neck flask.
2. In a separate flask, combine 0.063 g Se and 2.4 ml TOP and add a magnetic stir bar. The mixture of TOP and selenium should be degassed under vacuum for 30 min.
3. Degas ODA for 90 min at 120 °C, then put under Ar flow with a wide glass exhaust.
4. Heat ODA to 300 °C and, and inject Se mixture. Let temperature return to 300 °C.
5. Inject 1.0 ml of Et₂Zn (10% by wt. in hexane) to the reaction flask and allow to react at 265 °C for around 3 min, or until the exciton absorbance peak shifts to a desired wavelength (λ=350-400 nm), upon which remove the flask from the heating mantle.
6. Once the temperature of the reaction flask drops to ~60 °C, add 12 ml methanol and split between two 15-ml centrifuge tubes, topping off with methanol. Centrifuge for 5 min and pour off the liquid phase. Redissolve the precipitated nanocrystals in toluene and repeat.

2. Growth of CdS Rods on ZnSe Cores⁹

1. Combine 3.0 g TOPO, 0.280 g ODPA, 0.080 g HPA, and 0.090 g CdO and add a magnetic stir bar in a three neck flask.
2. In a separate flask, combine 0.120 g S, and 4.0 ml TOP and add a magnetic stir bar.
3. Degas CdO solution for 45 min at 150 °C and TOP for 45 min at 120 °C, then put under Ar flow with wide glass exhausts.
4. Heat the CdO solution to 380 °C until CdO is dissolved and solution is clear and colorless. Meanwhile, heat the S solution to 120 °C until S is dissolved and the mixture is clear and colorless.
5. Add all of the ZnSe from step 1 to the S solution.
6. Add 2.0 ml of TOP to the Cd solution and let the temperature return to 380 °C. Once 380 °C is reached, immediately inject the S solution into the Cd solution.
7. Allow the nanorods to grow for 6-9 min, including the temperature recovery time, and remove the flask from the heating mantle. The longer the solution is left on the heat, the longer the rods will be.
8. Product may be a green gel, add chloroform to liquefy and split into two vials.
9. Precipitate nanocrystals in ethanol, pour off the liquid phase, and redissolve the precipitated nanocrystals in chloroform.

3. Growth of Pt Tip on CdS Rods¹⁰

1. Combine 0.2 ml OA, 0.2 ml oleylamine, 10 ml diphenyl ether, and 43 mg 1,2-hexadecanediol and add a magnetic stir bar in a flask.
2. Degas the mixture for 1 hr at 80 °C, then put under Ar flow and increase temp to 200 °C.
3. Add a mixture of CdS rods in chloroform and 20 mg Pt (II) acetylacetonate. After 5-7 min of the reaction mixture being at 190 °C, the solution will turn black. Remove the flask from the heat.
4. Precipitate nanocrystals in a 10:3 mixture of methanol to chloroform with a centrifuge and pour off the liquid phase. Redissolve the precipitated crystals in chloroform and repeat.

4. Ligand Exchange with MUA¹¹

1. In a vial, disperse nanorods in 10 ml chloroform.
2. Add 0.1 g MUA to the nanorod solution and sonicate until all the MUA is dissolved.
3. In a separate vial, dissolve 0.1 g KOH in 20 ml triple distilled water (TDW).
4. Add approximately 5.0 ml of the TDW solution to the nanorod solution and shake vigorously.
5. Centrifuge the mixture from step 4.4 at 6000 rpm for 1 min to separate the aqueous and organic phases.
6. Collect the top (aqueous) phase and add methanol to achieve a solution that is 3:1 methanol to water.
7. Centrifuge the mixture from step 4.6 at 6000 rpm for 2 min to precipitate nanocrystals. Pour off the liquid phase and redisperse the precipitated crystals by sonicating in TDW.
8. If the organic phase in step 4.5 still retains some of the color of the original nanocrystal solution, repeat steps 4.4 through 4.7.

5. Synthesis of PbS Cores (Adapted from ref.¹²)

1. Combine 0.49 g PbO, 18 ml ODE, and 1-16 ml OA (Depending on desired size, more OA yields larger particles) and add a magnetic stir bar in a three neck flask.
2. In a separate flask, add 10 ml ODE and a magnetic stir bar.
3. Degas both flasks for 1 hr at 120 °C, then put under Ar flow.
4. Heat the Pb solution to 135 °C. Meanwhile, cool the flask containing only ODE to room temperature.
5. Add 0.21 ml TMS to the room temperature ODE, then inject the mixture into the Pb solution at 135 °C.
6. Heat the mixture at 135 °C for 1-5 min (depending on desired size, longer heating yields larger particles), and place into an ice bath to quench the reaction.
7. Precipitate nanocrystals in distilled acetone, pour off the liquid phase, and redissolve precipitated crystals in toluene. Repeat two more times.

6. Growth of CdS Shell on PbS Cores¹³

1. Combine 1.0 g CdO, 6 ml OA, and 15 ml ODE and add a magnetic stir bar in a three neck flask.
2. In a separate flask add 20-40 mg of PbS cores dissolved in toluene and a magnetic stir bar.
3. Heat the CdO solution to 280 °C until the solution is clear and colorless, then cool to 100 °C.
4. Heat the PbS solution to 110 °C for no more than 5 min to boil off excess, but not all, solvent, then inject the Cd solution.
5. Slowly heat the reaction mixture to 120-160 °C (depending on the desired shell thickness). For thinner shells (1-2 monolayers) quench the reaction immediately after the injection of the Cd solution.
6. Once desired temperature is reached, quench the reaction by placing the flask in an ice bath.
7. Precipitate crystals in ethanol, pour off the liquid phase, and redissolve the precipitated crystals in toluene. Repeat twice. On final cleaning cycle, redissolve and store the crystals in anhydrous octane.

7. Preparation of TiO₂ on FTO/Glass Substrates

1. Hand wash the FTO coated glass with detergent (Alconox) and rinse with deionized water.
2. Sonicate the glass in methanol, acetone, then isoproponal, for 5 min each and dry with Ar flow.
3. Place the glass in a bath of 75 mM TiCl₄ in deionized water and heat (in air) for 30 min at 70 °C.
4. Rinse the glass with deionized water and dry with Ar, then heat (in air) at 450 °C for 1 hr and let cool to room temperature.
5. While the glass is cooling, dissolve TiO₂ Dyesol paste in terpinol in a 3:1 ratio by weight.
6. Place 3 drops of the TiO₂ mixture on the center of the FTO side of a dry glass slide that has been treated with TiCl₄ and spin for 6 sec at 700 rpm and 1 min at 2,000 rpm.
7. Anneal the slide in air at 450-500 °C until the film turns brown, then clear.

8. Spin Coating PbS/CdS into a Film

1. All spin coating steps are performed in an argon glovebox.
2. Place 4-5 drops of PbS/CdS in octane (10 mg/ml) onto a still slide from step 7 and let spread until the center begins to dry, then spin for 5 sec at 600 rpm then 15 sec at 2,500 rpm.
3. Place 10 drops of a 1:3 MPA:methanol solution on the slide, fully covering the surface, and spin for 5 sec at 600 rpm, then 15 sec at 2,500 rpm.
4. Wash surface with methanol by placing 10 drops on the slide and spinning for 5 sec at 600 rpm, then 15 sec at 2,500 rpm.
5. Wash surface with octane by same method as in step 8.4.
6. Repeat steps 8.2-8.5 for each subsequent layer of the film.
7. Anneal the film after every third layer at 150 °C for 15 min. The final film should have an absorbance near 1.5 at the wavelength of the peak of the NC.

9. Dip Coating PbS/CdS Films

1. Prepare a solution of 0.43 g cadmium acetate in 80 ml methanol in a beaker large enough to completely submerge the sample.
2. Prepare a solution of sodium sulfide nonahydrate (Na₂S•9H₂O) in 80 ml methanol in a beaker large enough to completely submerge the sample.
3. Submerge the sample for 1 min in the Cadmium bath, and rinse with methanol. Then submerge for 1 min in the Sulfer bath, and rinse with methanol.
4. Repeat step 9.3 until pores are filled (generally 4-8 times).
5. Anneal sample at 150 °C for 15 min.

10. Treating Films with CTAB¹⁴

1. Place 0.25 ml of CTAB, dissolved in methanol, at a concentration of 10 mg/ml, on film from step 9 and let sit for 1 min, then spin at 2,500 rpm for 30 sec.
2. Rinse slide with 10 drops of methanol and spin until dry.
3. Repeat 10.1 and 10.2 once.

11. Representative Results

The evolution of the absorption and emission spectra corresponding to ZnSe/CdS/Pt NCs during each step of the synthesis is tracked in Figure 1. It can be seen that Figure 1b expresses absorbance peaks at ~350 nm and ~450, characteristic of ZnSe and CdS respectively, and, most notably, now displays the onset of a FL peak at ~550 nm. This FL feature is a result of emissive excitonic decay across the ZnSe/CdS interface. This type II interdomain FL is then quenched by the growth of the Pt tip (Figure 1c), due to the rapid injection of the delocalized electron into the metal moiety. This ultra-fast charge separation enables the utilization of the electron for the photocatalytic reduction of water. Hydrophilic MUA ligands are then added to facilitate the removal of the hole from the ZnSe domain, increasing stability by inhibiting oxidation of the semiconductor core, allowing for the sustained reduction of solar H₂ (Figure 2). As a result of hole scavenging, the organic ligands become susceptible to photodegradation, but this can be simply mitigated by the addition of fresh ligands, as seen in Figure 2. Thus, the introduction of hydrophylic ligands not only render the NCs water soluble, but they also adjust the energetics of the system to protect the nanostructure at the cost of the inexpensive, easy to replace organic surfactants.

For PbS/CdS nanocrystal solids, Figure 3a and 3b shows a schematic of the fabrication process and the final device. Figure 3c, a TEM image of the core/shell nanocrystals, shows that the CdS infiltrates evenly around the PbS core. The nanocrystal solid is shown to be relatively free of pores in Figure 3d, an SEM image of the cross-section of a device. One result of the shell growth, that is observable, is a blueshift in both the absorbance and emission peaks. This shift is attributed to the PbS core shrinking as the Cd ions infiltrate further into the core, and can be seen in Figure 4. A large increase in the emission can also be seen in Figure 4, due to the enhanced quantum confinement provided by the CdS shell. The CdS layer not only increases the emission, it also protects the core, increasing the thermal stability of the solid, up to almost 200 °C, almost 50 °C higher than a PbS nanocrystal solid alone. Solar cells constructed using this nanocrystal solid architecture have not only shown better thermal stability, but have also been shown to have higher open circuit voltages (as high as 0.7 V) than the related organically linked films. These films have also shown a much higher tolerance to oxygen atmospheres, lasting for several days in normal atmospheric conditions with no degradation.

Figure 1. Optical properties of fabricated heteronanocrystals. (a). The absorbance of ZnSe NCs showing an excitonic feature at λ = 390 nm. Bandage emission was not observed for these samples. (b). Emission and absorbance of ZnSe/CdS nanorods grown from ZnSe core NCs. (c). Absorbance of ZnSe/CdS nanorods after Pt deposition.

Figure 2. Evolution of hydrogen production on MUA capped ZnSe/CdS/Pt heteronanocrystals. The hydrogen production is resumed upon addition of new ligands to the ZnSe/CdS/Pt nanoparticles. The H2 production rate (the slope of the new experimental curve) after addition of fresh ligands (8-12 hr) is approximately the same as prior to the initial degradation (0-8 hr).

Figure 3. Schematic representation of (a) the steps involved in fabrication of Nanocrystal solids and (b) the final photovoltaic device. Below are SEM images of (c) PbS/CdS core/shell nanocrystals and (d) a side view of the nanocrystal solid.

Figure 4. Changes in the absorption (bottom) and emission (top of PbS NCs resulting from the deposition of approximately 1 monolayer of the CdS shell. The shrinking of the PbS core from the cation exchange is reflected as a ≈150 nm shift in both spectra. The PbS fluorescence intensity is enhanced due to the formation of type 1 heterostructure.

Figure 5. Schematic representation of energy level alignment in (a) ZnSe/CdS/Pt core/rod/tip structures and (b) ZnTe/CdS/Pt core/rod/tip structures. Choosing appropriate materials is of the utmost importance in these devices, as holes from ZnTe seeded structures sit in an energy level that makes traveling to the ligand unfavorable.