An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature
Please note that all translations are automatically generated. Click here for the English version.

Una tecnica disponibile per la preparazione del nuovo Cast MnCuNiFeZnAl lega con Superior servizio capacità e ad alta temperatura di smorzamento

6,759 Views

•

14:51 min

•

September 23, 2018

DOI:

10.3791/57180-v

DOI:
10.3791/57180-v

•

14:51 min
September 23, 2018

•

1 Views
, , , , ,
1School of Manufacturing Science and Engineering,Sichuan University, 2機械工学科,Hong Kong Polytechnic University, 3Department of Mechanical and Electrical Engineering,Chengdu Aeronautic Polytechnic

概要

Automatically generated

Qui presentiamo un protocollo per ottenere un romanzo basati su Mn-Cu lega con eccellenti prestazioni complete di una tecnologia di fusione di alta qualità e metodi di trattamento termico ragionevole.

Explore More Videos

Cast MnCuNiFeZnAl AlloyDamping CapacityHigh Service TemperatureVacuum Induction MeltingSand Mold CastingHeat TreatmentMicrostructureManganese-copper Based AlloysFace-centered Cubic To Face-centered Tetragonal Phase TransformationAging TreatmentNanoscale Precipitates

Read Article

Cite this Article

Li, D., Liu, W., Li, N., Zhong, Z., Yan, J., Shi, S. An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature. J. Vis. Exp. (139), e57180, doi:10.3791/57180 (2018).