High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

Please note that all translations are automatically generated. Click here for the English version.

によってナノ構造イットリア安定化ジルコニア（YSZ）足場の高温製作<em>その場での</em>カーボンテンプレート化キセロゲル

DOI:

10.3791/55500-v

•

07:13 min

•

April 16, 2017

•

Sixbert P. Muhoza, Matthew A. Cottam, Michael D. Gross²

¹Department of Chemistry,Wake Forest University, ²Center for Energy, Environment, and Sustainability,Wake Forest University

Capitoli

00:05Titolo
00:44Preparing Xerogel Pellets
03:04Sintering the Xerogel Pellet in an Inert Atmosphere
03:45Determining Carbon Template Concentration
04:32Preparing High Surface Area YSZ Scaffold by Carbon Template Removal
05:02Results: Fabrication of Porous, Nanostructured YSZ Scaffolds
06:29Conclusion

Summary

Traduzione automatica

1000℃及び1400℃の間の温度で多孔質、ナノ構造イットリア安定化ジルコニア（YSZ）足場を製造するためのプロトコルが提供されます。

Tags

Nanostructured Ceramics Yttria-stabilized-zirconia (YSZ)Carbon Templating Xerogels High-temperature Fabrication Surface Area Mixed Metal Oxide Materials Zirconium Chloride Glucose Yttrium Nitrate Propylene Oxide Gelation Solvent Exchange Drying Xerogel Powder Pellet Pressing

Article

Embed

AGGIUNGI ALLA PLAYLIST

Usage Statistics

Video correlati

製造、ち密化、および3Dカーボンナノチューブの微細構造のレプリカ成形

シリカ超高品質ファクターMicroresonatorsの作製

半導体技術との互換性低温カーボンナノチューブ垂直相互接続の作製

バルクヘテロ接合太陽電池の印刷作製と<em>その場で</em>形態キャラクタリゼーション

3Dカーボンマイクロエレクトロメカニカルシステム（C-MEMS）の製作

その場でテスト用 LiPON ベース固体リチウムイオン Nanobatteries の集束イオンビームビーム加工

静的スキャンモードで中性子ガンマ解析による土壌炭素の測定

Ex その場その場で調査構造変換の方法: 金属ガラスの結晶化の事例

高周波マグネトロンスパッタリングによる GdBa₂Cu₃O₇₋_δ/チタン酸ストロンチウム₃ (STO) 単結晶基板上 La_0.67Sr_0.33MnO₃準二層フィルム

ハイブリッドスマートセンサーの作製のための印刷

Read Article