High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

Høj temperatur Fabrikation af nanostrukturerede yttriastabiliseret-Zirconia (YSZ) Stilladser ved<em> In Situ</em> Carbon Templatering Xerogeler

DOI:
10.3791/55500-v

•

07:13 min

•

April 16, 2017

•

, ,
1Department of Chemistry,Wake Forest University, 2Center for Energy, Environment, and Sustainability,Wake Forest University

Capitoli

  • 00:05Titolo
  • 00:44Preparing Xerogel Pellets
  • 03:04Sintering the Xerogel Pellet in an Inert Atmosphere
  • 03:45Determining Carbon Template Concentration
  • 04:32Preparing High Surface Area YSZ Scaffold by Carbon Template Removal
  • 05:02Results: Fabrication of Porous, Nanostructured YSZ Scaffolds
  • 06:29Conclusion

Summary

Traduzione automatica

Traduzione automatica

En protokol til fremstilling af porøse, nanostrukturerede yttriastabiliseret-zirconia (YSZ) scaffolds ved temperaturer mellem 1000 ° C og 1400 ° C er præsenteret.

Tags

Nanostructured CeramicsYttria-stabilized-zirconia (YSZ)Carbon TemplatingXerogelsHigh-temperature FabricationSurface AreaMixed Metal Oxide MaterialsZirconium ChlorideGlucoseYttrium NitratePropylene OxideGelationSolvent ExchangeDryingXerogel PowderPellet Pressing

Article

Embed

AGGIUNGI ALLA PLAYLIST

Usage Statistics

Video correlati

Fabrication, fortætning og Replica Molding af 3D kulstof nanorør mikrostrukturer

Fabrikation af Silica Ultra High Quality-Factor Microresonators

Fabrikation af lav temperatur kulstof nanorør Lodrette Interconnect Kompatibel med Semiconductor Technology

Udskrivning Fabrikation af Bulk heterojunction solceller og<em> In Situ</em> Morfologi Karakterisering

Fremstilling af 3D-carbon-mikroelektromekaniske systemer (C-MEMS)

Fokuseret Ion Beam fabrikation af LiPON-baseret Solid-state Lithium-ion Nanobatteries til In Situ test

Målinger af kulstof i jorden af Neutron-Gamma analyse i statisk og Scanning tilstande

Metoder til Ex Situ og In Situ undersøgelser af strukturelle forandringer: sagen om krystallisering af metalliske briller

Radio Frequency Magnetron Sputtering af GdBa2Cu3O7−δ/ La0,67Sr0,33MnO3 kvasi tolagede film på SrTiO3 (STO) Single-krystal substrater

Hybrid udskrivning for fabrikation af Smart sensorer

Read Article