An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature

Uma técnica disponível para a preparação de novos MnCuNiFeZnAl liga fundido com Superior serviço de capacidade e de alta temperatura de amortecimento

6,759 Views

•

14:51 min

•

September 23, 2018

DOI:

10.3791/57180-v

DOI:
10.3791/57180-v

•

14:51 min
September 23, 2018

•

1 Views
, , , , ,
1School of Manufacturing Science and Engineering,Sichuan University, 2Department of Mechanical Engineering,Hong Kong Polytechnic University, 3Department of Mechanical and Electrical Engineering,Chengdu Aeronautic Polytechnic

Summary

Automatically generated

Aqui nós apresentamos um protocolo para obter um romance baseados em Mn-Cu liga com excelentes performances abrangentes por uma tecnologia de fundição de alta qualidade e métodos de tratamento de calor razoável.

Explore More Videos

Cast MnCuNiFeZnAl AlloyDamping CapacityHigh Service TemperatureVacuum Induction MeltingSand Mold CastingHeat TreatmentMicrostructureManganese-copper Based AlloysFace-centered Cubic To Face-centered Tetragonal Phase TransformationAging TreatmentNanoscale Precipitates

Read Article

Cite this Article

Li, D., Liu, W., Li, N., Zhong, Z., Yan, J., Shi, S. An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature. J. Vis. Exp. (139), e57180, doi:10.3791/57180 (2018).

Download .ris file

Copy

Share Video

.

Copy