Dry Oxidation and Vacuum Annealing Treatments for Tuning the Wetting Properties of Carbon Nanotube Arrays
JoVE Revista
Ingeniería
Se requiere una suscripción a JoVE para ver este contenido.  Inicie sesión o comience su prueba gratuita.
JoVE Revista Ingeniería
Dry Oxidation and Vacuum Annealing Treatments for Tuning the Wetting Properties of Carbon Nanotube Arrays

Dry Oxidation and Vacuum Annealing Treatments for Tuning the Wetting Properties of Carbon Nanotube Arrays

DOI:
10.3791/50378-v

•

08:59 min

•

April 15, 2013

•

,
1Graduate Aeronautical Laboratories,California Institute of Technology

Capítulos

  • 00:05Título
  • 01:40Carbon Nanotube Array Growth
  • 04:02Oxygen Adsorption Induced by UV/Ozone Treatment
  • 04:53Oxygen Adsorption Induced by Oxygen Plasma Treatment
  • 05:42Oxygen Desorption Induced by Vacuum Annealing Treatment
  • 06:43Results: Variation of Wetting Behavior of Carbon Nanotube Arrays with Oxygen Adsorption and Desorption
  • 08:30Conclusion

Summary

Traducción Automática

Traducción Automática

This article describes a simple method to fabricate vertically aligned carbon nanotube arrays by CVD and to subsequently tune their wetting properties by exposing them to vacuum annealing or dry oxidation treatment.

Tags

Carbon Nanotube ArraysWetting PropertiesHydrophilicHydrophobicDry OxidationVacuum AnnealingSurface ChemistryOxygen AdsorbatesFunctionalizationSuperhydrophobic

Article

Embed

Añadir a la lista de reproducción

Usage Statistics

Videos relacionados

Fabrication, Densification, and Replica Molding of 3D Carbon Nanotube Microstructures

Synthesis and Functionalization of Nitrogen-doped Carbon Nanotube Cups with Gold Nanoparticles as Cork Stoppers

Fine-tuning the Size and Minimizing the Noise of Solid-state Nanopores

Ambient Method for the Production of an Ionically Gated Carbon Nanotube Common Cathode in Tandem Organic Solar Cells

Fabrication of Low Temperature Carbon Nanotube Vertical Interconnects Compatible with Semiconductor Technology

Development of an Experimental Setup for the Measurement of the Coefficient of Restitution under Vacuum Conditions

Seedless Growth of Bismuth Nanowire Array via Vacuum Thermal Evaporation

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

Precision Milling of Carbon Nanotube Forests Using Low Pressure Scanning Electron Microscopy

Orientational Transition in a Liquid Crystal Triggered by the Thermodynamic Growth of Interfacial Wetting Sheets

Read Article