Özet

불균일 PR-도핑 된 SrTiO3의 합성<sub> 3</sub> 도자기와 그 열전 특성

Published: August 15, 2015
doi:

Özet

A protocol for the synthesis and processing of polycrystalline SrTiO3 ceramics doped non-uniformly with Pr is presented along with the investigation of their thermoelectric properties.

Abstract

We demonstrate a novel synthesis strategy for the preparation of Pr-doped SrTiO3 ceramics via a combination of solid state reaction and spark plasma sintering techniques. Polycrystalline ceramics possessing a unique morphology can be achieved by optimizing the process parameters, particularly spark plasma sintering heating rate. The phase and morphology of the synthesized ceramics were investigated in detail using X-ray diffraction, scanning electron microcopy and energy-dispersive X-ray spectroscopy. It was observed that the grains of these bulk Pr-doped SrTiO3 ceramics were enhanced with Pr-rich grain boundaries. Electronic and thermal transport properties were also investigated as a function of temperature and doping concentration. Such a microstructure was found to give rise to improved thermoelectric properties. Specifically, it resulted in a significant improvement in carrier mobility and the thermoelectric power factor. Simultaneously, it also led to a marked reduction in the thermal conductivity. As a result, a significant improvement (> 30%) in the thermoelectric figure of merit was achieved for the whole temperature range over all previously reported maximum values for SrTiO3-based ceramics. This synthesis demonstrates the steps for the preparation of bulk polycrystalline ceramics of non-uniformly Pr-doped SrTiO3.

Introduction

산화물 열전은 전자 수송 특성에 대한 안정성 및 비용 관점에서 고온 열전 애플리케이션을위한 유망한 후보로 나타났다. n 형 산화물 열전기 중에서 고농도 도핑 된 티탄산 스트론튬 (STO)를 인해 흥미로운 전기적 성질에 많은 관심을 끌고있다. 그러나, 큰 총 열 전도성 (κ ~ 12 W M -1 K -1 (300) 단결정에 대한 K에서) (1)과 낮은 캐리어 이동도 (μ ~ 6cm 2 V -1-1 단결정 300 K에서) 한 악영향 메리트 차원 도면에 의해 평가된다 열전 성능에 영향을 미치는, 도전율 σ α는 제벡 계수이고, ZT = α이 σT / κ는, T 켈빈 절대 온도, 총 열전도율 κ. 우리는 본원에서 역률 같은 분자를 정의 PF = α 263; T. (SiGe와 합금과 같은) 다른 고온 열전기과 경쟁이 산화물 열전 재료 위해서는, 역률 및 / 또는 격자 열 전도도의 감소에 더 현저한 증가가 요구된다.

STO의 열전 특성을 향상시키기 위해 실험 연구의 대부분은 주로 변형 필드와 포논의 질량 변동 산란 통한 열전도율의 감소에 초점을 맞추고있다. 이러한 시도는 다음을 포함한다 : (i) 단일 또는 이중의 Sr 도핑 2+ 또는 / 및 Ti 4+ 사이트,이 방향에 대하여 주된 노력으로서, 자연 초 격자 Ruddlesden-포퍼 구조의 2,3- (II)의 합성 상기 나노 크기의 제 2상의 SrO를 첨가하여 층, (4) 및 (iii) 복합 공학 절연막을 통해 열전 도성을 감소시키기 위해. 5 단, 최대 최근까지 더 개선 전략 substant보고되지 않았다ially 이들 산화물에 열전 역률을 증가시킨다. 벌크 단일 및 다결정 STO에서보고 된 최대 역률 (PF) 값 PF <1.0 m의 W -1 K -1의 상한에 국한되어왔다.

합성 방법 및 처리 기술의 다양한 시도 상기 아이디어를 구현하는 데 사용되어왔다. 분말 합성 경로는 종래의 고상 반응을 포함 6 졸겔 7 종래 소결 반면 열수, 8 및 연소 합성, 9, 6 핫 프레스 (10)와 최근에 방전 플라즈마 소결 (12)로 분말을 조밀화하는데 사용되는 공통 기술들이다 대량 도자기. 그러나 유사한 불순물 (예를 들어, 라)와 도핑 농도, 그 결과 대량 세라믹 전자 및 열 수송 특성의 범위를 나타낸다. 이는 된 SrTiO3 <공정의 강하게 의존 결함 화학 대형 인합성에 의존하는 특성을 초래 부> 3. 열전 전송 혜택을 합성 및 처리 매개 변수를 최적화 보고서의 소수는있다. 그것은 때문에 아주 작은 포논에 SrTiO3를 무료 경로 (300 K에서 L 산도 ~ 2 나노 미터)을 의미하는 것으로 언급 할 가치가있다, 11 나노 구조는 주로 감소를 통해 대량 STO 도자기의 TE 성능의 개선을위한 실행 가능한 옵션이 아니다 격자 열 전도도.

최근에, 우리는 동시에 강화 된 화력 요인에서 발생하는 비 균일 PR-도핑 된 SrTiO3 3 도자기의 장점의 열전 그림의 30 % 이상 향상을보고이 상세한 비디오 프로토콜에서 열전도. 12, 13 감소, 우리가 제시하고 이들의 제조에 대한 우리의 합성 전략의 단계 논의 향상된 전자 및 열전 특성을 나타내는 STO 세라믹스 잠을 도핑.

Protocol

PR-도핑 된 SrTiO3 3 분말 1. 준비 SrCO 3 분말 (7.53407 G), 이산화 티탄 나노 분말 (4.28983 G), 및 PR의 이론 양, 산화 티타늄 3 잠 0.05 0.95 시니어 분말 10g을 준비 무게를하기 위해 2 O 반응 다음의 3 소결 덩어리 (0.44299 G) X = 0.05에 대한 : </…

Representative Results

X 선 회절 패턴 된 SrTiO3으로 된 SrTiO3에 잠의 용해도가 3 격자 PR-도핑의 효과를 연구하기 위하여 같은 제조 된 분말 및 PR 함량의 함수로서 대응하는 벌크 세라믹스 (도 1)에 대해 수집 된 3 차 위상 (들)의 형성. 패턴은 반사 공간 군 (도 1a)와 입방 격자에 연동 될 수있는 모든 같이 제조 된 분말의 SrTiO3를 위상의 형성을 확인한다. 홍보 컨텐츠를 증가 (…

Discussion

이 프로토콜에서, 우리는 성공적으로 향상된 전자 및 열전 특성을 나타내는 벌크 다결정 PR-도핑 된 SrTiO3를 세라믹을 제조하기 위해 합성 전략의 단계를 제안 하였다. 프로토콜의 주요 단계는 하이로로서 준비된 분말을 치밀화 (I) 대기압 방전 플라즈마 소결법의 기능 (ⅱ) 복용 이점을 공기에 도핑 된 SrTiO3 3 분말의 고상 합성을 포함 벌크 세라믹스 동시에 밀도는 더 잠 가진 샘플?…

Açıklamalar

The authors have nothing to disclose.

Acknowledgements

The authors wish to acknowledge the competitive faculty-initiated collaboration (FIC) grant from KAUST.

Materials

SrCO3 Powder, 99.9% Sigma Aldrich 472018
TiO2 Nanopowder, 99.5% Sigma Aldrich 718467
Pr2O3 Sintered Lumps, 99.9% Alfa Aesar 35663 
Name of  Equipment
Spark Plasma Sintering  Dr. Sinter Lab SPS-515S
Resistivity/Seebeck Coefficient Measurement System Ulvac-Riko ZEM-2
Laser Flash Thermal Diffusivity Measurement System Netzsch LFA-457 Microflash
Differential Scanning Calorimetry (DSC) System Netzsch 404C Pegasus
Physical Property Measurement system (PPMS) Quantum Design
Field Emission Scanning Electron Microscope (FE-SEM) Hitachi SU-6600
Energyy-dispersive X-ray Spectroscopy (EDS) Oxford Instruments
X-ray Diffractometer Rigaku Ultima IV
Bench-top Sputter Coater Denton Vacuum Desk II
Diamond  Wheel Saw South Bay Technology

Referanslar

  1. Ohta, S., Nomura, T., Ohta, H., Koumoto, K. High-temperature Carrier Transport and Thermoelectric Properties of Heavily La-or Nb-doped SrTiO3 Single Crystals. J. Appl. Phys. 97, (2005).
  2. Wang, H. C., et al. Enhancement of Thermoelectric Figure of Merit by Doping Dy in La0.1Sr0.9TiO3 Ceramic. Mater. Res. Bull. 45, 809-812 (2010).
  3. Bhattacharya, S., Mehdizadeh Dehkordi, A., Alshareef, H. N., Tritt, T. M. Synthesis–Property Relationship in Thermoelectric Sr1−xYbxTiO3−δ Ceramics. J. Phys. D: Appl. Phys. 47, 385302 (2014).
  4. Wang, Y., Lee, K. H., Ohta, H., Koumoto, K. Thermoelectric Properties of Electron Doped SrO(SrTiO3)n (n=1,2) Ceramics. J. Appl. Phys. 105, 1037011-1037016 (2009).
  5. Wang, N., et al. Effects of YSZ Additions on Thermoelectric Properties of Nb-Doped Strontium Titanate. J. Electron. Mater. 39, 1777-1781 (2010).
  6. Muta, H., Kurosaki, K., Yamanaka, S. Thermoelectric Properties of Rare Earth Doped SrTiO3. J. Alloys Compd. 350, 292-295 (2003).
  7. Shang, P. -. P., Zhang, B. -. P., Li, J. -. F., Ma, N. Effect of Sintering Temperature on Thermoelectric Properties of La-doped SrTiO3 Ceramics Prepared by Sol-gel Process and Spark Plasma Sintering. Solid State Sciences. 12, 1341-1346 (2010).
  8. Wang, Y., Fan, H. J. Sr1-xLaxTiO3 Nanoparticles: Synthesis, Characterization and Enhanced Thermoelectric Response. Scripta Materialia. 65, 190-193 (2011).
  9. Kikuchi, A., Okinakab, N., Akiyama, T. A Large Thermoelectric Figure of Merit of La-doped SrTiO3 Prepared by Combustion Synthesis with Post-Spark Plasma Sintering. Scripta Materialia. 63, 407-410 (2010).
  10. Obara, H., et al. Thermoelectric Properties of Y-Doped Polycrystalline SrTiO3.Jpn. J. Appl. Phys. 43, L540-L542 (2004).
  11. Koumoto, K., Wang, Y., Zhang, R., Kosuga, A., Funahashi, R. Oxide Thermoelectric Materials: A Nanostructuring Approach. Annu. Rev. Mater. Res. 40, 363-394 (2010).
  12. Mehdizadeh Dehkordi, A., et al. Large Thermoelectric Power Factor in Pr-Doped SrTiO3−δ Ceramics via Grain-Boundary-Induced Mobility Enhancement. Chem. Mater. 26, 2478-2485 (2014).
  13. Mehdizadeh Dehkordi, A., Bhattacharya, S., He, J., Alshareef, H. N., Tritt, T. M. Significant Enhancement in Thermoelectric Properties of Polycrystalline Pr-doped SrTiO3 Ceramics Originating from Nonuniform distribution of Pr dopants. Appl. Phys. Lett. 104, 1939021-1939024 (2014).
  14. . . Standard Test Methods for Density of Compacted or Sintered Powder Metallurgy (PM) Products Using Archimedes’ Principle. , (2015).
  15. Parker, W. J., Jenkins, R. J., Butler, C. P., Abbott, G. L. Flash Method of Determining Thermal Diffusivity, Heat Capacity and Thermal Conductivity. J. Appl. Phys. 32, 1679-1684 (1961).
  16. Cowan, R. D. Pulse Method of Measuring Thermal Diffusivity at High Temperatures. J. Appl. Phys. 34, 926-927 (1963).
  17. Mehdizadeh-Dehkordi, A. . An Experimental Investigation Towards Improvement of Thermoelectric Properties of Strontium Titanate Ceramics. , (2014).
  18. . . DSC Pegasus 404C Operating Manual. , (1999).
  19. Daw, J. E. Measurement of Specific Heat Capacity Using Differential Scanning Calorimeter. Report of US Department of Energy. , (2008).
  20. Tritt, T. M. . Thermal Conductivity: Theory, Properties and Applications. , (2004).
  21. . . SC7610 Sputter Coater Operating Manual. , (2002).
  22. Tritt, T. M., Rowe, D. M. Electrical and Thermal Transport Measurement Techniques for Evaluation of the figure-of-Merit of Bulk Thermoelectric Materials. Thermoelectrics Handbook: Macro to Nano. , 23-1-23-17 (2006).
  23. Burkov, A. T., Rowe, D. M. Measurements of Resistivity and Thermopower: Principles and Practical Realization. Thermoelectrics Handbook: Macro to Nano. , 22-1 (2006).
  24. . . Physical Property Measurement System: AC Transport Option User’s Manual. , (2003).
  25. Ohta, S., Ohta, H. Grain Size Dependence of Thermoelectric Performance of Nb-doped SrTiO3. Polycrystals. J. Ceram. Soc. Jpn. 114, 102 (2006).
  26. Wang, N., He, H., Ba, Y., Wan, C., Koumoto, K. Thermoelectric Properties of Nb-doped SrTiO3 Ceramics Enhanced by Potassium Titanate Nanowires Addition. J. Ceram. Soc. Jpn. 118, 1098 (2010).
  27. Ohta, S., et al. Large Thermoelectric Performance of Heavily Nb-doped SrTiO3 Epitaxial Film at High Temperature. Appl. Phys. Lett. 87, 092108 (2005).
  28. Kovalevsky, A., Yaremchenko, A., Populoh, S., Weidenkaff, A., Frade, J. Enhancement of Thermoelectric Performance in Strontium Titanate by Praseodymium Substitution. J. Appl. Phys. 113, 053704 (2013).
  29. Kovalevsky, A. V., et al. Towards a High Thermoelectric Performance in Rare-Earth Substituted SrTiO3: Effects Provided by Strongly-Reducing Sintering Conditions. Phys. Chem. 16, 26946 (2014).
  30. Dawson, J. A., Tanaka, I. Local Structure and Energetics of Pr- and La-Doped SrTiO3 Grain Boundaries and the Influence on Core–Shell Structure Formation. J. Phys. Chem. C. 118, 25765-25778 (2014).
  31. Mehdizadeh Dehkordi, A., et al. New Insights on the Synthesis and Electronic Transport in Bulk Polycrystalline Pr-doped SrTiO3−δ. Appl. Phys. Lett. 117, 055102 (2015).

Play Video

Bu Makaleden Alıntı Yapın
Mehdizadeh Dehkordi, A., Bhattacharya, S., Darroudi, T., Zeng, X., Alshareef, H. N., Tritt, T. M. Synthesis of Non-uniformly Pr-doped SrTiO3 Ceramics and Their Thermoelectric Properties. J. Vis. Exp. (102), e52869, doi:10.3791/52869 (2015).

View Video