Note: This protocol requires special care in the handling of nanomaterials. As-purchased single-walled carbon nanotubes (SWNTs) exist in the form of fine powder and thus, they should be considered as nano-hazardous materials before dispersing them in aqueous solutions. Please use appropriate safety equipment described in the material safety data sheets (MSDS).
1. Preparation of Poloxamer 407/SWNT Aqueous Suspensions
Note: Proceed with all the sample preparation procedures at a lower temperature than the critical micellization temperature (CMT) of the block copolymers used. The poloxamer 407/SWNT samples were prepared at 20 °C, below the CMT of poloxamer 407 (30 °C).21
2. Extended Q-range Small-angle Neutron Scattering (EQ-SANS) Measurements
Note: To work at the beamlines of Spallation Neutron Source (SNS), an accepted beamtime proposal is required. Radiological safety training and other instrument specific training are also required in advance. Access and training details are provided by the SNS User Office and can be found at neutrons.ornl.gov.
3. SANS Data Reduction and Analysis
4. Real-space Observation Using Atomic Force Microscopy (AFM)
Poloxamer 407-coated SWNT nanorod suspensions were fabricated using the sample preparation procedure (Figure 4), which can be divided into two important processes; the physical adsorption process of poloxamer 407 on SWNT surfaces using ultra-sonication, and the fractionation process of individually-stabilized SWNTs from bundled aggregates using centrifugation.
The SANS scattering intensities were obtained for the prepared poloxamer 407/SWNT/D2O sample in a temperature range of 20-60 °C in the absence (Figure 5A) and presence (Figure 5B) of 5MS. The scattering intensities with the q–1 behavior in the low q regions (< 0.02 Å–1) indicate the existence of cylindrical rod-like particles in the aqueous media. By changing the temperature from 20 °C to 60 °C or by adding 5MS additives, the scattering intensities show clear changes; a shift to higher q in the intermediate q-region (0.02-0.05 Å–1) and the development of a peak at high q (about 0.11 Å–1) are observed. These analogous changes due to temperature-control and 5MS-addition originate from the structural change of poloxamer 407-encapsulation layer on SWNTs. As summarized in Figure 6A-6D, the CNT core/hydrophobic inner shell/hydrated poloxamer 407 layer undergoes a structural transformation from an SWNT encapsulated by spherical micelles of poloxamer 407 at room temperature to an SWNT encapsulated by a compact cylindrical layer of poloxamer 407 at higher temperature. The structural change was reversible with varying temperature regardless of the existence of 5MS additives; the size of hydrated polymer blobs was reversibly controlled in a temperature range between 20 °C and 60 °C. During this structural change of the poloxamer 407 layer, the spherical poloxamer 407 micelle with a radius of gyration of 45 Å, which consists of several poloxamer 407 chains, becomes a set of single-chain blobs which surround the SWNT core more compactly with a radius of gyration of 30 Å.
The structural change upon both temperature control and aromatic additives is explicable by variations in intermolecular interactions among polymers, water, and SWNTs. Increasing hydrophobicity of PPO and PEO blocks with increasing temperature causes stronger interaction of adsorbed polymers with SWNT core surfaces than with water.21 As a result, the adsorbed polymers form more compact encapsulation layer at high temperature to cover the hydrophobic core more efficiently and reduce the interfacial free energy. This tendency can be more promoted in the presence of 5MS, because of the preferential interaction between SWNT and a benzene ring of 5MS as well as the strong tendency of 5MS to bind with poloxamer 407.21,22 Especially, the inner shell thickness (Figure 6B), which was measured to be about 3 Å close to the planar distance between 5MS molecules and SWNT surfaces,21 is in good agreement with the prediction that the added 5MS prefer to occupy the SWNT surface area and provide a friendly interface to the polymers.
As a complementary investigation to the SANS study, the poloxamer 407/SWNT nanorods were observed in real space using an AFM. Figures 7A and 7B are tapping mode AFM images of poloxamer 407/SWNT nanorods which were spin-coated onto a Si-wafer. Although these AFM images only show a dried morphology of the nanorods without water, they provide evidence of de-bundling and dispersion of SWNTs as well the length distribution of the nanorods.
Figure 1. Snapshot of the ultrasonication process for SWNT stabilization. A sample tube is put into a water bath with the tip dipped in. Please click here to view a larger version of this figure.
Figure 2. Aluminum banjo cell holder for the EQ-SANS experiment at SNS. (A) Disassembled parts including (i) a banjo cell (ii) spacers, and (iii) a holder. (B) Assembled parts. Please click here to view a larger version of this figure.
Figure 3. Standard EQ-SANS experiment environments. (A) Sample booth, and (B) control software at the beam line. Please click here to view a larger version of this figure.
Figure 4. Simplified sample preparation procedure for Poloxamer 407/SWNT (sample #1) and Poloxamer 407/SWNT/5MS (sample #2) suspensions. The mass ratio between SWNTs and Poloxamer 407 in these final suspensions was measured by thermogravimetric analysis (TGA) after freeze-drying (*). (This figure has been modified with permission from ref. 21. Copyright 2015, American Chemical Society.) Please click here to view a larger version of this figure.
Figure 5. SANS intensities measured in a temperature range from 20 °C to 60 °C. (A) Poloxamer 407/SWNT/D2O sample. (B) Poloxamer 407/SWNT/5MS/D2O sample. The solid lines are the curves obtained by fitting the SANS data using a modified core/shell/chain model. The q–1 behavior at low q regions around 0.01 Å–1 indicates the existence of rod-like particles in the suspensions. The curves have been shifted for clarity. (This figure has been modified with permission from ref. 21. Copyright 2015, American Chemical Society.) Please click here to view a larger version of this figure.
Figure 6. Detailed structures of encapsulation layers from a SANS model fit analysis. (A) Radius of gyration (Rg) of poloxamer 407 chain blobs and (B) thickness of hydrophobic inner shell layers (T1) on SWNT surfaces in the absence (diamond) and presence (square) of 5-Methylsalicylic acid (5MS) in a temperature range from 20 °C to 60 °C. Rg was reversibly changed by controlling temperature via heating (filled marker) and cooling (filled marker with a cross inside) processes regardless of the existence of 5MS. (C-D) Schematic cross-sectional diagrams suggested from SANS analysis for the poloxamer 407/SWNT nanorods at room temperature (top) and its structural changes with increasing temperature or adding additives (bottom). (This figure has been modified with permission from ref. 21. Copyright 2015, American Chemical Society.) Please click here to view a larger version of this figure.
Figure 7. Tapping mode AFM images of spin-coated Poloxamer 407/SWNT nanorods on Si-wafer. (A) The height channel image provides the z-directional thickness information. (B) The tapping amplitude channel image presents clear boundaries of deposited nanoparticles. Scale bar: 1 µm. (This figure has been modified with permission from ref. 21. Copyright 2015, American Chemical Society.) Please click here to view a larger version of this figure.
HiPco Single-walled carbon nanotubes | Unidym | P2771 | |
Pluronic F127 | BASF | 9003-11-6 | Mw = 12.6 kg/mol |
5-methylsalicylic acid | TCI America | C0410 | |
Ultrasonic processor | Cole-Parmer | ML-04714-52 | |
Sorvall 6 plus centrifuge | Thermo Scientific | 46910 | |
Innova AFM | Bruker | ||
Si-wafer | Silicon Quest International | 150 mm in diameter ; N type <1-1-1> cut ; 1-10 Ohm/cm ; Single-side polyshed (675 +- 25 um) ; Diced (12 mm x 12 mm) |
We demonstrate a protocol for single-walled carbon nanotube functionalization using thermo-sensitive PEO-PPO-PEO triblock copolymers in an aqueous solution. In a carbon nanotube/PEO105-PPO70-PEO105 (poloxamer 407) aqueous solution, the amphiphilic poloxamer 407 adsorbs onto the carbon nanotube surfaces and self-assembles into continuous layers, driven by intermolecular interactions between constituent molecules. The addition of 5-methylsalicylic acid changes the self-assembled structure from spherical-micellar to a cylindrical morphology. The fabricated poloxamer 407/carbon nanotube hybrid particles exhibit thermo-responsive structural features so that the density and thickness of poloxamer 407 layers are also reversibly controllable by varying temperature. The detailed structural properties of the poloxamer 407/carbon nanotube particles in suspension can be characterized by small-angle neutron scattering experiments and model fit analyses. The distinct curve shapes of the scattering intensities depending on temperature control or addition of aromatic additives are well described by a modified core-shell cylinder model consisting of a carbon nanotube core cylinder, a hydrophobic shell, and a hydrated polymer layer. This method can provide a simple but efficient way for the fabrication and in-situ characterization of carbon nanotube-based nano particles with a structure-tunable encapsulation.
We demonstrate a protocol for single-walled carbon nanotube functionalization using thermo-sensitive PEO-PPO-PEO triblock copolymers in an aqueous solution. In a carbon nanotube/PEO105-PPO70-PEO105 (poloxamer 407) aqueous solution, the amphiphilic poloxamer 407 adsorbs onto the carbon nanotube surfaces and self-assembles into continuous layers, driven by intermolecular interactions between constituent molecules. The addition of 5-methylsalicylic acid changes the self-assembled structure from spherical-micellar to a cylindrical morphology. The fabricated poloxamer 407/carbon nanotube hybrid particles exhibit thermo-responsive structural features so that the density and thickness of poloxamer 407 layers are also reversibly controllable by varying temperature. The detailed structural properties of the poloxamer 407/carbon nanotube particles in suspension can be characterized by small-angle neutron scattering experiments and model fit analyses. The distinct curve shapes of the scattering intensities depending on temperature control or addition of aromatic additives are well described by a modified core-shell cylinder model consisting of a carbon nanotube core cylinder, a hydrophobic shell, and a hydrated polymer layer. This method can provide a simple but efficient way for the fabrication and in-situ characterization of carbon nanotube-based nano particles with a structure-tunable encapsulation.
We demonstrate a protocol for single-walled carbon nanotube functionalization using thermo-sensitive PEO-PPO-PEO triblock copolymers in an aqueous solution. In a carbon nanotube/PEO105-PPO70-PEO105 (poloxamer 407) aqueous solution, the amphiphilic poloxamer 407 adsorbs onto the carbon nanotube surfaces and self-assembles into continuous layers, driven by intermolecular interactions between constituent molecules. The addition of 5-methylsalicylic acid changes the self-assembled structure from spherical-micellar to a cylindrical morphology. The fabricated poloxamer 407/carbon nanotube hybrid particles exhibit thermo-responsive structural features so that the density and thickness of poloxamer 407 layers are also reversibly controllable by varying temperature. The detailed structural properties of the poloxamer 407/carbon nanotube particles in suspension can be characterized by small-angle neutron scattering experiments and model fit analyses. The distinct curve shapes of the scattering intensities depending on temperature control or addition of aromatic additives are well described by a modified core-shell cylinder model consisting of a carbon nanotube core cylinder, a hydrophobic shell, and a hydrated polymer layer. This method can provide a simple but efficient way for the fabrication and in-situ characterization of carbon nanotube-based nano particles with a structure-tunable encapsulation.