Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars
JoVE Journal
Ingegneria
È necessario avere un abbonamento a JoVE per visualizzare questo.  Accedi o inizia la tua prova gratuita.
JoVE Journal Ingegneria
Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars
Please note that all translations are automatically generated. Click here for the English version.

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars

DOI:
10.3791/57859-v

•

10:24 min

•

November 01, 2018

•

, , ,
1Department of Civil Engineering,Shenzhen University, 2Guangdong Province Key Laboratory of Durability for Marine Civil Engineering,Shenzhen University, 3Department of Engineering and the Built Environment,Anglia Ruskin University

Capitoli

  • 00:04Titolo
  • 01:15Initial Specimen Testing
  • 05:00Specimen Corrosion and Subsequent Testing
  • 07:41Results: Comparison of Measurement Methods
  • 09:14Conclusion

Summary

Traduzione automatica

Traduzione automatica

This paper measures the geometry and the amount of corrosion of a steel bar using different methods: mass loss, calipers, drainage measurements, 3D scanning, and X-ray micro-computed tomography (XCT).

Tags

Corrosion MeasurementSteel BarSurface Morphology3D ScanningXCTVernier CaliperDrainage MeasurementMass LossCross-sectionUniversal Testing Machine

Article

Embed

AGGIUNGI ALLA PLAYLIST

Usage Statistics

Video correlati

Mechanical Expansion of Steel Tubing as a Solution to Leaky Wellbores

폭발 정량화는 홉 킨슨 압력 막대를 사용하여

소설 재료의 저온 Magnetotransport 측정을위한 고급 실험 방법

형상 기억의 조사를 기반으로 Elastocaloric 냉각 프로세스 및 모델 검증을위한 실험 방법

햇빛에 노출 된 표면에 실리카 나노 입자 - 폴리 에스테르 코팅의 진화

단방향 직물에 대한 테스트를 심지 : 모세관 매개 변수의 측정은 액체 복합 성형 공정에서 모세관 압력을 평가하는

레이저 조사 형 광열 열 분석을 이용한 구조 가열에 의한 지층 결함 국산화

Preparation and High-temperature Anti-adhesion Behavior of a Slippery Surface on Stainless Steel

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior

DP780 강철의 마찰 교반 점 용접을 통해 랩 조인트 생성

Read Article